Tungsten trioxide (WO 3 ) has been widely regarded as a prospective bifunctional material due to its electrochromic and pseudocapacitive properties, while still facing the dilemma of inadequate cycle stability and trapping-induced degradation. Here, inspired by the trees-strengthening approach, a unique titanium dioxide (TiO 2 ) nanorod arrays strengthened WO 3 nano-trees (TWNTs) heterojunction was rationally designed and constructed. In sharp contrast to the transmittance modulation (ΔT) attenuation of primary WO 3 nano-trees during cycling, the TWNTs film showed not only excellent electrochromic performance but also fascinating cycle stability (77.35% retention of the initial ΔT after 10,000 cycles). Besides, the trapping-induced degradation could be easily rejuvenated by a potentiostatic de-trapping process. An electrochromic energy storage device (EESD) was further assembled based on the TWNTs film to deliver excellent ΔT (up to 79.5% at 633 nm), fast switching speed (t c /t b =1.9 s/14.8 s), extremely high coloration efficiency value (443.4 cm 2 •C −1 ), and long-term cycle stability (over 10,000 charge/discharge cycles). This innovative study provided in-depth insights into the electrochromism nature and a significant step in the realization of stable electrochromic-energy storage application, paving the way for multifunctional smart windows as well as next-generation optoelectronic devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.