Most research on nanocrystalline alloys has been focused on planned doping of metals with other metallic elements, but nonmetallic impurities are also prevalent in the real world.
Photoluminescence properties have been connected to intrinsic point defects for Si abundant (red bar) and N plentiful (blue bars) α-Si3N4via band structure modelling using DFT calculations.
Ultra-long, single crystal, Eu-doped α-Si3N4 nanowires were prepared by a simple approach involving nitriding Eu-doped cryomilled nanocrystalline Si powder in NH3 flow at 1350 °C for 4 h. Phases, chemical composition and microcosmic feature of cryomilled powders and as-prepared nanowires were tested by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), respectively. The results suggested that Eu was successfully introduced into Si lattice after the cryomilling process and then entered into the lattice of α-Si3N4 during the nitridation process. The as-synthesized Eu-doped α-Si3N4 nanowires had highly uniform dimension with 20~30 nm in diameter and ~100 μm in length. The room temperature photoluminescence (PL) spectrum of as-synthesized nanowires showed a broad band emission center at 570 nm which was attributed to the transition from 4f65d to 4f7 in Eu2+. The transition from Eu3+ to Eu2+ during nitridation process was tested by X-ray photoelectron spectroscopy (XPS).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.