In order to reduce the dependency of resin synthesis on petroleum resources, vanillyl alcohol which is a renewable material that can be produced from lignin has been used to synthesize bioepoxy resin. Although it has been widely reported that the curing reaction and properties of the cured epoxies can be greatly affected by the molecular structure of the curing agents, the exact influence remains unknown for bioepoxies. In this study, four aliphatic amines with different molecular structures and amine functionalities, namely triethylenetetramine (TETA), Tris(2-aminoethyl)amine (TREN), diethylenetriamine (DETA), and ethylenediamine (EDA), were used to cure the synthesized vanillyl alcohol–based bioepoxy resin (VE). The curing reaction of VE and the physicochemical properties, especially the thermomechanical performance of the cured bioepoxies with different amine functionalities, were systematically investigated and compared using different characterization methods, such as DSC, ATR–FTIR, TGA, DMA, and tensile testing, etc. Despite a higher curing temperature needed in the VE–TETA resin system, the cured VE–TETA epoxy showed a better chemical resistance, particularly acidic resistance, as well as a lower swelling ratio than the others. The higher thermal decomposition temperature, storage modulus, and relaxation temperature of VE–TETA epoxy indicated its superior thermal stability and thermomechanical properties. Moreover, the tensile strength of VE cured by TETA was 1.4~2.6 times higher than those of other curing systems. In conclusion, TETA was shown to be the optimum epoxy curing agent for vanillyl alcohol–based bioepoxy resin.
In recent years, China is increasingly dependent on imported wood. Afrormosia and Newtonia are some of the imported species with good utilization potential. However, both of them also have problems with poor dimensional stability. In order to make better use of these two types of wood, the influence of heat treatment under air and palm oil conditions on the color, dimensional stability, and hygroscopicity of Afrormosia and Newtonia was investigated. The Afrormosia and Newtonia wood samples were heated in air or palm oil medium for two hours at 160 °C, 180 °C and 200 °C, respectively. Then, the color, weight changes, swelling, moisture absorption and chemical structure were evaluated for each case. As results, the heat treatments with air or palm oil increased the dark color of Newtonia and Afrormosia wood and this increase was proportional to the treatment temperature. The tangential and radial swelling coefficient for air heat treatment of Afrormosia wood at 200 °C were, respectively, reduced by 24.59% and 19.58%, while this reduction for Newtonia was 21.32% and 14.80%. The heat treatment in palm oil further improved the stability and hygroscopicity of the wood, showing that the Afrormosia samples treated by palm oil at 200 °C underwent a decrease of its tangential and radial swelling coefficient, respectively, by 49.34% and 45.88%, whereas the tangential and radial swelling coefficient of Newtonia treated under the same conditions were reduced by 42.85% and 33.63%, respectively. The heat treatments of Afrormosia and Newtonia samples under air at 200 °C diminished the water absorption by 21.67% and 22.12%. The water absorption of Afrormosia and Newtonia heat-treated under palm oil at 200 °C was reduced, respectively, by 39.40% and 37.49%. Moreover, the FTIR analysis showed the decrease of hydroxyl groups in proportion to the wood treatment temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.