The high-temperature mechanical properties and microstructure of HK40 heat-resistant steel with different content of Al were investigated. The results from scanning electron microscope and transmission electron microscope showed that a large amount of spheroidal and dispersed γ′ phase were observed HK40 steel with 4.72wt.% and 7.10wt.% Al. The diameter of γ′ phase decreases from about 1.5μm to 50nm after solution treatment of 1200°C for 5h. The results of short term tensile test showed that tensile strength at 900°C decreased and the elongation was improved with increasing Al content. The oxides in the alloy with 4.72wt.% and 7.10wt.% Al were more uniform and finer than that in the alloy with and without 1.68wt.% Al.
The study deals with a wastewater treatment system which is combination of modified facultative anaerobic baffled reactor (MFABR) and an aerobic unit. The efficient decolorization and biological degradation of the wastewater that contains commercially important cationic red 2GL (azo) in the MFABR under facultative anaerobic conditions are the research focuses. The results indicate that over 95.2% decolorization and about 54.6% COD removal efficiency can be obtained in MFABR. High dye concentration (500 mg/L) still results in over 90.6% decolorization efficiency. The main characteristics of the process are highly efficient decolorization in MFABR and greatly reducing COD in aerobic unit.
The scoring process of mulberry fiber was studied in this paper, and through analyzing the impacts of scoring technological parameters to the degumming of mulberry fiber, finally, the optimum technological condition was determined. At the same time, the properties of the fiber were tested and studied.
Phenolic fiber is a new fiber and has excellent flame retardant properties. In order to investigate the textile possibility of phenolic fiber and to develop protective clothing and decorative fabrics containing phenolic fiber, the mechanical properties of phenolic fiber were studied firstly, then the polyester fiber was chosen to blend with different portion of phenolic fiber to enhance the strength of the blended yarn and finally the fabrics were knitted with different blended yarns. The strength and wear resistance of different blending ratio of phenolic/polyester blended yarn, and the bursting strength, abrasion resistance and flame retardant properties of the blended fabrics were analyzed and compared. The experimental results shows that the breaking tenacity and elongation at break are low, only 1.3 cN/dtex and 9.4%, respectively, which is not suitable for 100% phenolic fiber to be processed in yarn. The strength and wear resistance of the phenolic/polyester blend yarns and their knitted fabrics increase while the contents of polyester are increased. The flame retardant of phenolic/polyester blend fabrics is improved greatly due to phenolic fiber. Therefore, it is necessary for phenolic fiber to modify its strength and extension in order to be able to get the 100% phenolic yarn and products and in order to give full play to the excellent characteristics of the phenolic fiber.
For the purpose of recycling of cotton waste cuttings and exploring the prospect of preparation for super absorbent polymer (SAP), the high viscosity carboxymethyl cellulose (CMC) was made from cotton waste first and then the SAP was synthesized by grafting acrylic acid (AA) onto the CMC with the potassium persulfate being as initiator, N, N'-methylene bis acrylamide as crosslinker. The impact of polymerization temperature, time, initiator dosage, AA concentration, crosslinker dosage, and neutralization degree on water absorbency of SAP was studied. The optimum conditions are mass ratio of AA and CMC 7.11 g/g, initiator dosage 0.03 g/g CMC, crosslinker dosage 0.2 g/100g AA, neutralization degree 80% and polymerization time 1.5 h at 70°C of the polymerization temperature. The water retention of the polymer is good and the water absorbency reaches up to 702.5 g/g.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.