A type of polyester-based self-matting waterborne polyurethane (ESMWPU) with an excellent matte effect of 0.8° and transmittance of 78.5% for PVC artificial leather was synthesized. The influence of synthesis parameters, including R value, crosslinking and hydrophilic group content, on coating gloss and transmittance was investigated. Meanwhile, the properties necessary for applying water-based resins to plasticized PVC were detailed. The results demonstrated that R value, crosslinking degree and hydrophilic group content synergistically decided the morphological changes of latex particles during their film-forming process in three aspects: particle stiffness, three-dimensional structure and particle size, respectively. With optimized parameters of R = 1.9, TMP = 2 wt% and DMPA = 1.75 wt%, ESMWPU latex particles stabilized their spherical shapes without collapsing in the film-forming process and created a rough surface, resulting in a matte effect. In terms of application performance, good wetting and adhesion for ESMWPU to a plasticized PVC surface was achieved with a 2 wt% leveling agent load. Moreover, due to the high cohesion energy of ester bonds and intermolecular hydrogen bonds, this type of polyester-based ESMWPU also depicted admirable thermal adhesion resistance. All aforementioned results distinctly demonstrate a feasible yet promising paradigm for applying ESMWPU on PVC artificial leather.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.