The typical co-precipitation method was adopted to synthesized the Li-excess Li1.20[Mn0.52−xZrxNi0.20Co0.08]O2 (x = 0, 0.01, 0.02, 0.03) series cathode materials. The influences of Zr4+ doping modification on the microstructure and micromorphology of Li1.20[Mn0.52Ni0.20Co0.08]O2 cathode materials were studied intensively by the combinations of XRD, SEM, LPS and XPS. Besides, after the doping modification with zirconium ions, Li1.20[Mn0.52Ni0.20Co0.08]O2 cathode demonstrated the lower cation mixing, superior cycling performance and higher rate capacities. Among the four cathode materials, the Li1.20[Mn0.50Zr0.02Ni0.20Co0.08]O2 exhibited the prime electrochemical properties with a capacity retention of 88.7% (201.0 mAh g−1) after 100 cycles at 45 °C and a discharge capacity of 114.7 mAh g−1 at 2 C rate. The EIS results showed that the Zr4+ doping modification can relieve the thickening of SEI films on the surface of cathode and accelerate the Li+ diffusion rate during the charge and discharge process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.