Electromagnetic (EM) absorbing and shielding composites with tunable absorbing behaviors based on Ti3C2 MXenes are fabricated via HF etching and annealing treatment. Localized sandwich structure without sacrificing the original layered morphology is realized, which is responsible for the enhancement of EM absorbing capability in the X-band. The composite with 50 wt % annealed MXenes exhibits a minimum reflection loss of -48.4 dB at 11.6 GHz, because of the formation of TiO2 nanocrystals and amorphous carbon. Moreover, superior shielding effectiveness with high absorption effectiveness is achieved. The total and absorbing shielding effectiveness of Ti3C2 MXenes in a wax matrix with a thickness of only 1 mm reach values of 76.1 and 67.3 dB, while those of annealed Ti3C2 MXenes/wax composites are 32 and 24.2 dB, respectively. Considering the promising performance of Ti3C2 MXenes with the modified surface, this work is expected to open the door for the expanded applications of MXenes family in EM absorbing and shielding fields.
In this work, mesoporous carbon hollow microspheres (PCHMs) with designable mesoporous shell and interior void are constructed by a facile in situ stöber templating approach and a pyrolysis-etching process. The PCHMs are characterized by scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectra, Raman spectroscopy, and nitrogen adsorption and desorption system. A uniform mesoporous shell (pore size 4.7 nm) with a thickness of 55 nm and a cavity size of 345 nm is realized. The composite of paraffin mixed with 20 wt % PCHMs exhibits a minimum reflection coefficient (RC) of -84 dB at 8.2 GHz with a sample thickness of 3.9 mm and an effective absorption bandwidth (EAB) of 4.8 GHz below -10 dB (>90% electromagnetic wave is attenuated). Moreover, the composite of phenolic resin mixed with 20 wt % PCHMs exhibits an ultrawide EAB of 8 GHz below -10 dB with a thinner thickness of 2.15 mm. Such excellent electromagnetic wave absorption properties are ascribed to the large carbon-air interface in the mesoporous shell and interior void, which is favorable for the matching of characteristic impedance as compared with carbon hollow microspheres and carbon solid microspheres. Considering the excellent performance of PCHMs, we believe the as-fabricated PCHMs can be promising candidates as highly effective microwave absorbers, and the design philosophy can be extended to other spherical absorbers.
Three-dimensional (3D) flexible foams consisting of reduced graphene oxides (rGO) and in situ grown SiC nanowires (NWs) were prepared using freeze-drying and carbothermal reduction processes. By means of incorporating SiC nanowires into rGO foams, both the thermostability and electromagnetic absorption of the composites were improved. It was demonstrated that rGO/SiC NW foams were thermostable beyond ∼630 °C (90% weight retention in air atmosphere). As expected, rGO/SiC NW foams in the poly(dimethylsiloxane) matrix achieved effective absorption in the entire X-band (8.2-12.4 GHz) with a thinner thickness (3 mm) in comparison with those of the pure rGO foams. It is revealed that SiC nanowires with abundant stacking faults, twinning interfaces, and bridged junctions play an important role in the enhanced electromagnetic absorption performance, in addition to the contribution of interconnected graphene networks. Hierarchical rGO/SiC NW foams not only are efficient absorbers in the critical environments but also can be applied in photocatalytic and thermal-management fields.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.