The influence of the compensating cation (Na+, Li+, Mg2+) nature on the water adsorption properties of LTA and FAU-type zeolites was investigated. Cation exchanges were performed at 80 °C for 2 h using 1 M aqueous solutions of lithium chloride (LiCl) or magnesium chloride (MgCl2). XRF and ICP-OES analyses indicate that the cation exchange yields reach values between 59 to 89% depending on the number of exchange cycles and the nature of the zeolite and cation, while both zeolites structures are preserved during the process, as shown by XRD and solid state NMR analyses. Nitrogen adsorption-desorption experiments indicate a higher available microporous volume when sodium cations are replaced by smaller monovalent lithium cations or by divalent magnesium cations because twice less cations are needed compared to monovalent cations. Up to 15% of gain in the available microporous volume is obtained for FAU-type zeolites exchanged with magnesium cation. This improvement facilitates the adsorption of water with an increase in the water uptake up to 30% for the LTA and FAU type zeolites exchanged with magnesium. These exchanged zeolites are promising for uses in water decontamination because a smaller amount is needed to trap the same amount of water compared to their sodium counterparts.
The influence of the charge compensating cation nature (Na+, Mg2+) on the water adsorption properties of LTA-type zeolites used as filler in composite materials (zeolite/polymers) was investigated. Large scale cation exchanges were performed on zeolite powder at 80 °C for 2 h using 1 M magnesium chloride (MgCl2) aqueous solutions. XRF, ICP, and EDX analyses indicate a successful cationic exchange process without the modification of the zeolite structure as shown by XRD and solid-state NMR analyses. Composite materials (granulates and molded parts) were manufactured using to extrusion and injection processes. In the case of MgA zeolite, nitrogen adsorption–desorption experiments allowed us to measure a microporous volume, unlike NaA zeolite, which is non-porous to nitrogen probe molecule. SEM and EDX analyses highlighted the homogeneous distribution of zeolite crystals into the polymer matrix. Water adsorption capacities confirmed that the trends observed in the zeolite powder samples are preserved after dragging zeolites into composite formulations. Granulates and molded parts composite samples containing the magnesium exchanged zeolite showed an increase of their water adsorption capacity up to +27% in comparison to composite samples containing the non-exchanged zeolite. The MgA composite is more promising for water decontamination applications due to its higher water adsorption properties than the NaA composite.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.