This work is concentrated on plasma sprayed cermet coatings consisting of stainless steel (SS) (17 wt % Cr and 12 wt % Ni) and chromium oxide (Cr2O3). These powders were sprayed simultaneously, however being injected separately to account for the drastic difference in their thermo-physical properties. Chromium oxide was injected internally and stainless steel externally. The plasma parameters (arc current, hydrogen vol %, mass flow rate) were optimized as well as the injector positions. Coatings were achieved with different mass ratios of SS and Cr2O3. All exhibited a lamellar structure with well distributed Cr2O3 and SS lamellae. They were then systematically characterized by their phase content (XRD), composition (EDS), Vickers micro hardness, morphology (SEM), slurry and dry wear resistances. Finally the best dry linear abrasion resistance was obtained for the pure chromium oxide coatings, while the best slurry wear resistance corresponded to coatings with a mass ratio SS/ Cr2O3 of 56/44.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.