CoCrNi equiatomic medium entropy alloy sheets were prepared by asymmetric rolling, cryorolling, and asymmetric cryorolling. The asymmetric cryorolled samples exhibited a noteworthy ultra-fine-grain heterogeneous lamella structure. The microstructure and corresponding hardness obtained by different rolling processes and subsequent annealing are compared. It can be seen from the results that the cryogenic deformation temperature had a stronger effect on the mechanical properties of the medium entropy alloys (MEA), compared with the shear strain caused by the asymmetric cryorolling. The effect of annealing temperature on texture components and volume fractions of the specially rolled samples was also analyzed. The result revealed that the recrystallized MEA exhibited similar texture components and the corresponding volume fraction, which indicated that the rolling process had limited influence on the formation of annealing texture. The recrystallized texture after annealing retained the deformation texture and twin related orientations appeared. Asymmetric rolled MEA showed strong random composition than symmetric rolled MEA regardless of rolling temperature. The recrystallized textures of the species obtained by the three rolling processes did not exhibit a significant dependence on the annealing temperature.
High-purity (99.999%) nickel with lamellar-structure grains (LG) was obtained by room-temperature rolling and cryorolling in this research, and then annealed at different temperatures (75 °C, 160 °C, and 245 °C). The microstructure was characterized by transmission electron microscopy. The grain growth mechanism during annealing of the LG materials obtained via different processes was studied. Results showed that the LG high-purity nickel obtained by room-temperature rolling had a static discontinuous recrystallization during annealing, whereas that obtained by cryorolling underwent static and continuous recrystallization during annealing, which was caused by the seriously inhibited dislocation recovery in the rolling process under cryogenic conditions, leading to more accumulated deformation energy storage in sheets.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.