Additive manufacturing (AM) is a rapidly growing field of technology. In order to increase the variety of metal alloys applicable for AM, selective laser melting (SLM) of duplex stainless steel 2205 powder and the resulting microstructure, density, mechanical properties, and corrosion resistance were investigated. An optimal set of processing parameters for producing high density (>99.9%) material was established. Various post-processing heat treatments were applied on the as-built predominantly ferritic material to achieve the desired dual-phase microstructure. Effects of annealing at temperatures of 950 °C, 1000 °C, 1050 °C, and 1100 °C on microstructure, crystallographic texture, and phase balance were examined. As a result of annealing, 40–46 vol.% of austenite phase was formed. Annealing decreased the high yield and tensile strength values of the as-built material, but significantly increased the ductility. Annealing also decreased the residual stresses in the material. Mechanical properties of the SLM-processed and heat-treated materials outperformed those of conventionally produced alloy counterparts. Using a scanning strategy with 66° rotation between layers decreased the strength of the crystallographic texture. Electrochemical cyclic potentiodynamic polarization testing in 0.6 M NaCl solution at room temperature showed that the heat treatment improved the pitting corrosion resistance of the as-built SLM-processed material.
Hydrogen solubility and diffusion in austenitic stainless steels, namely AISI 310, AISI 301LN and AISI 201, are studied with thermal desorption spectroscopy (TDS) after electrochemical potentiostatic hydrogen pre‐charging. Temperature dependencies of hydrogen desorption for all studied steels manifest a complex main peak caused by hydrogen releasing from the steel lattice by diffusion. Depending on the steel and heating rate the peak is situated from 350 to 500 K and its shape reflects a specific of hydrogen diffusion in stainless steels, which are multicomponent alloys. Analysis of the TDS curves is based on the hydrogen diffusion model taking into account trapping of hydrogen atoms in the energetically deep interstitial positions in the steel crystal lattice. Diffusion coefficient of hydrogen and its total content after the same charging procedure are obtained from the TDS curves and compared for the studied steels.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.