BackgroundPrevious studies on the use of SO2 and CO2 as impregnating agent for sugar cane bagasse steam treatment showed comparative and promising results concerning the cellulose enzymatic hydrolysis and the low formation of the inhibitors furfural and hydroxymethylfurfural for the use of CO2 at 205°C/15 min or SO2 at 190°C/5 min. In the present study sugar cane bagasse materials pretreated as aforementioned were analyzed by scanning and transmission electron microscopy (SEM and TEM), X-Ray Diffraction (XRD) and Infrared (FTIR spectroscopy) aiming a better understanding of the structural and chemical changes undergone by the pretreated materials.ResultsSEM and TEM data showed that the structural modifications undergone by the pretreatment with CO2 were less pronounced in comparison to that using SO2, which can be directly related to the combined severity of each pretreatment. According to XRD data, untreated bagasse showed, as expected, a lower crystallinity index (CI = 48.0%) when compared to pretreated samples with SO2 (CI = 65.5%) or CO2 (CI = 56.4%), due to the hemicellulose removal of 68.3% and 40.5%, respectively. FTIR spectroscopy supported SEM, TEM and XRD results, revealing a more extensive action of SO2.ConclusionsThe SEM, TEM, XRD and FTIR spectroscopy techniques used in this work contributed to structural and chemical analysis of the untreated and pretreated bagasse. The images from SEM and TEM can be related to the severity of SO2 pretreatment, which is almost twice higher. The crystallinity index values obtained from XRD showed that pretreated materials have higher values when compared with untreated material, due to the partial removal of hemicellulose after pretreatment. FTIR spectroscopy supported SEM, TEM and XRD results. CO2 can actually be used as impregnating agent for steam pretreatment, although the present study confirmed a more extensive action of SO2.
Lignocellulosic plant cell wall is considered a potential source for second generation biofuels. The plant cell wall is a highly complex structure mainly composed of cellulose, hemicelluloses, and lignin that form a network of crosslinked fibers. The structural organization of the sugarcane cell wall has not been previously analyzed in detail, and this analysis is a prerequisite for further studies on the recalcitrance and deconstruction of its biomass. In this work, cellulose and lignin localization were investigated by confocal laser scanning microscopy. In addition, the internode sugarcane cell wall structural organization was analyzed by electron microscopy. Internode stem anatomy showed a typical monocot structure consisting of epidermis, hypoderm, and vascular bundles scattered throughout ground parenchyma tissue and surrounded by sclerenchyma fibers. Confocal images of safranin labeled sugarcane showed that lignin distribution was predominant in the vessel elements, cell wall corners (CC), and middle lamella (ML), while cellulose-rich cell walls were randomly distributed in the ML and organized in the other cell wall layers. KMnO4 cytochemistry revealed that lignin was predominantly distributed in secondary cell walls, ML and CC. Cell wall sublayers (S1, S2, and S3) were identified and measured by transmission electron microscopy. Our results provide insights that may help further understanding of sugarcane cell wall organization, which is crucial for the research and technology of plant-based biofuel production.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.