We have fabricated the BiCuSeO bulks using raw materials with Bi or Se deficiencies in the nominal composition and investigated crystallographic, chemical compositional, and thermoelectric properties. Owing to the Bi or Se deficiencies in the starting composition, excessive elements and related compounds were deposited as impurity phases and the matrix phase is nearly the stoichiometric BiCuSeO phase. The electrical resistivity, q(T), of the bulks decreases and thermoelectric power, S(T), also decreases with increasing the contents of Bi or Se deficiencies in the starting composition in spite of the stoichiometric matrix phase. These results strongly suggest that, from the X-ray photoelectron spectroscopy measurements, the actual oxidation states of Bi and Cu deviate from the formal valences of stoichiometric Bi 3þ Cu 1þ Se 2À O 2À . The introduction of a small amount of Bi and Se vacancies is also suggested. As a result, mobile carriers are introduced and the q and S values are changed. The maximum thermoelectric dimensionless figure of merit of ZT ¼ 0.60 was achieved at 773 K for the Bi 1-x CuSeO samples (x ¼ 0.025 and 0.05) in the starting composition. These results are in clear contrast with the reported results for the Cu deficiency bulks. Using these results, we propose charge valence equations and the origin of the carriers in the present BiCuSeO bulks and discuss the influence of created carriers on the thermoelectric properties.Published by AIP Publishing. https://doi.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.