This paper presents the test results of reinforced-concrete (RC) slabs strengthened with carbon-fibre-reinforced polymer (CFRP) sheets and exposed to a corrosive environment. Nine slab specimens (1500 × 700 × 100 mm) were constructed and subjected to accelerated corrosion exposure. Test variables included the clear concrete cover (10, 25 and 40 mm), the longitudinal reinforcing bar diameter (8, 10 and 12 mm) and different degrees of corrosion. The corresponding current and concrete corrosion cracks were continually monitored throughout the corrosion process. A decrease in the clear concrete cover increased the corrosion crack width and the cracking time of slab specimens to levels higher than those resulting from an increase in the reinforcing bar diameter. All slab specimens were tested to failure in four-point bending, to investigate the load-carrying capacity and average crack spacing of each corroded slab specimen. In addition, some reinforcing bars were extracted, to determine the loss in the steel mass when varying the clear concrete cover and the reinforcing bar diameter. The study reported in this paper thus establishes the effects of the clear concrete cover and the reinforcing bar diameter on corrosion activity in CFRP-strengthened RC slabs.
We report test results from an experimental study to investigate the effectiveness of carbon fiber-reinforced polymer (CFRP) against reinforcing steel bar corrosion. Twelve reinforced-concrete pile specimens of 180 mm square by 1,600 mm long were cast. Three pile specimens were corroded to 5% steel mass loss and then strengthened with CFRP sheets; four specimens were strengthened by using CFRP sheets, whereas the remaining five specimens were not strengthened. The specimens were placed in a simulated marine environment, and corrosion was induced by an impressed current technique. At different theoretical corrosion degrees, nondestructive tests were performed to investigate the corrosion activity of the pile specimens, and destructive tests were performed to determine reinforcing steel bar mass loss. Based on the findings, the effectiveness of the CFRP-strengthened RC piles under aggressive marine environmental conditions was established.
Please refer to published version for the most recent bibliographic citation information. If a published version is known of, the repository item page linked to above, will contain details on accessing it.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.