In the present paper, the leaching of copper from printed circuit boards (PCBs) using sulfuric acid with Cu2+ and O2 is proposed. The effects of various process parameters such as agitation speed, temperature, the type and the flow rate of gas, initial Cu2+ concentration, and pulp density were investigated to examine the dissolution behavior of Cu from PCBs in 1 mol/L sulfuric acid. The kinetic studies were performed using the obtained leaching data. The leaching rate of Cu from PCBs was found to be higher on addition of Cu2+ and O2 to the leachant in comparison with the addition of O2 or both Cu2+ and N2 in the leachant. The leaching efficiency of Cu was found to be increased with increasing agitation speed, temperature, O2 flow rate, and initial Cu2+ concentration and decreasing pulp density. The 96% of Cu leaching efficiency was obtained under the following conditions: sulfuric acid concentration, 1 mol/L; temperature, 90 °C; agitation speed, 600 rpm; pulp density, 1%; initial Cu2+ concentration, 10,000 mg/L; and O2 flow rate, 1000 cc/min. The leaching data and analyses indicate that the Cu leaching from PCBs followed the reaction-controlled model satisfactorily and determined that the activation energy was found to be 23.8 kJ/mol. Therefore, these results indicate that the sulfuric acid solution with Cu2+ and O2 as a mild leach medium without strong oxidants such as HNO3, H2O2, and Fe3+ is valid for Cu leaching from PCBs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.