A lot of dye pollutants were released in the aquatic environment as waste from industrial coloring process. This research aimed to study silica gels (SG) as a potential adsorbent to remove the dyes. The SG can be synthesized from coal fly ash (FA), which is industrial solid waste rarely utilized, using the sol-gel method. Its properties were then characterized by FTIR, XRD, SEM, and isothermal ads-des N2.As a result, FTIR spectra and XRD diffractogram exhibited the successfully SG synthesized from FA with the amorphous structure. The image analysis using SEM demonstrated that SG particles are spherical. The isotherm type, based on isotherm ads-des N2, is type II without hysteresis loop which represents the nonporous material SG with the surface area and pore diameter of 25.977 m 2 /g and 1.52 nm, respectively. The adsorption capacity performance of SG to remove methylene blue (MB) as a basic dye is 62.70 % which is higher than FA, following Langmuir isotherm adsorption model. The kinetics of adsorption rate of SG are based on the pseudo second order models accelerated by 3.37 times faster than FA.
AbstrakAbu terbang batu bara dengan prosentase kandungan SiO2 telah berhasil digunakan sebagai bahan baku pembuatan Silika Gel. Karakteristik silika gel diketahui dengan munculnya gugus fungsi silanol dan siloksan dengan FTIR, struktur kristal tak beraturan (amorf) dengan XRD, bentuk partikel bola (spherical) dan analisis unsur dengan EDX. Silika gel yang dihasilkan masih mengandung sedikit pengotor oksida alumina dan oksida natrium. Pengujian kapasitas adsorpsi Rhodamin-B silika gel lebih besar dibandingkan abu terbang dengan model adsorsi keduanya mengikuti model isotermal Langmuir dengan konsentrasi optimum pada 200 ppm. Kinetika adsorpsi mengikuti model Pseudo Second Order dimana laju adsorpsi silika gel sedikit lebih tinggi dibanding abu terban, tepai perbedaaanya tidak signifikan. [6]. Namun, penggunaan abu terbang secara langsung baik untuk beton maupun adsorben memberikan permasalahan karena kandung logam berat beracun seperti As, Ba, Hg, Cr, Ni, V, Pb, Zn and Se dapat dilepaskan ke lingkungan [7].Penghilangan logam pengotor yang beracun dan pemurnian kadar SiO2 pada abu terbang merupakan solusi yang menjanjikan untuk meningkatkan pemanfaatan silika sebagai adsorben. Mengacu pada kandungan SiO2 pada abu sekam padi dan baggas tebu yang dapat dimurnikan menjadi material silika gel dengan kemurnian 98-99% [8] dan [9], maka abu terbang juga dapat diubah menjadi silika gel. Pada penelitian sebelumnya [10], silika gel berhasil disintesis dari abu terbang yang memiliki kapasitas adsorpsi terhadap zat warna metilen biru meningkat 62,70% dibanding abu terbang. Kemampuan adsorpsi silika gel dipengaruhi oleh gugus silanol (Si-OH) dan gugus siloksan (Si-O-Si) pada permukaannya yang reaktif. terhadap polutan kationik [11]. Selain itu, struktur kerangka 3 dimensi tak beraturan (struktur amorf) juga berperan dalam proses adsorpsi [12].Limbah zat warna merupakan salah satu jenis limbah yang secara estetika dapat mengganggu lingkungan dan juga beracun bagi manusia dan hewan. Limbah zat warna dapat menghambat cahaya matahari masuk dalam sistem perairan, maka proses biologis dalam lingkungan perairan tidak dapat berjalan baik [13]. Jumlah produksi zat warna setiap tahun mencapai 7 x 10 5 ton dan sekitar 10-15 % akan dibuang ke sistem perairan [14]. Limbah zat warna dihasilkan dari aktifitas industri seperti tekstil, printing, kosmetik, dan pewarna makanan [15]. Salah satu jenis zat warna yang banyak digunakan dalam aktifitas industri adalah Rhodamin-B yang merupakan zat warna merah yang merupakan warna dasar.Tujuan dalam penelitian ini adalah untuk mempelajari kemampuan adsorpsi Rhodamin-B oleh silika gel yang di sintesis dari abu terbang batu bara. Pengujian variasi konsentrasi Rhodamin-B untuk menentukan model dan kapasitas adsorpsi silika gel terhadap Rhodamin-B.BERKALA SAINSTEK 2018, VI (1): 31-35
Synthesis of ZIF-8 (zeolitic Imidazolate Frameworks-8) have been successfully carried out by the reaction of zinc nitrate and 2-methylimidazolate in DMF (N'N-dimethylformamide) solvent at a temperature of 120 °C for 24 hours. Synthesis of ZIF-8 has been conducted five times with variations molar ratio of metal (Zn2+):ligand (MeIM) consecutive 1:1; 1:1.5; 1:2; 1:2.5 and 1:3 to study the influence of metal-ligand ratio of the crystallinity and morphology of ZIF-8 that was produced. The results of characterization by X-ray diffraction, FTIR and SEM show that ZIF-8 is synthesized with a ratio of metal: ligand = 1:2 showed the highest crystallinity and has the most irregular surface morphology with form box.
TiO2 anatase mesopori (ukuran pori 2-50 nm) memiliki aktivitas fotokatalitik yang besar. Metode sintesis kimia padat dapat digunakan sebagai alternatif untuk memperoleh TiO2 anatase dari natrium titanat dengan menggunakan prekursor yang murah berupaTiO2 rutile komersial. Surfaktan CTABr (Cetyltrimethylammonium Bromide) mampu menghasilkan TiO2 anatase mesopori dengan kemampuannya sebagai template atau agen pembentuk pori. Penelitian ini bertujuan mengetahui pengaruh variasi penambahan CTABr terhadap distribusi ukuran pori, volume total pori, luas permukaan TiO2 dan dan aktivitas fotokatalitik TiO2 hasil sintetis. Sintesis dilakukan menggunakan metode reaksi kimia padat dengan penambahan variasi perbandingan mol CTABr dan tanpa penambahan CTABr sebagai pembanding. Karakterisasi menggunakan XRD (X- Ray Powder Difraction), SEM (Scanning Electron Microscopy) dan Gas Sorption Analyer (GSA) untuk mengetahui struktur, morfologi dan sifat pori TiO2. TiO2 anatase mesopori hasil sintesis diaplikasikan sebagai fotokatalis dalam mendegradasi metilen biru. Hasil penelitian ini menunjukkan bahwa TiO2 anatase mesopori berhasil didapatkan dengan morfologi partikelnya berbentuk seperti balok, sisi tidak seragam serta ukuran partikel berkisar 200-500 nm. Variasi penambahan CTABr tidak memberikan pengaruh yang signifikan terhadap distribusi ukuran pori, volume total pori, luas permukaan dan aktivitas fotokatalitik dari TiO2 anatase mesopori, dengan hasil distribusi pori mayoritas pada 2 nm dan aktivitas fotokatalitik sekitar 77%
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.