In the recent two decades, Cr2+:ZnSe crystals have been widely used as a gain media for 2∼3 μm mid-infrared lasers. However, it still remains a huge challenge for researchers to meet more and more requirements on the crystals with high qualities and large sizes. In this work, one Cr2+:ZnSe single crystal with a diameter of about 15 mm was successfully grown by chemical vapor transporting (CVT) with NH4Cl in a closed quartz ampoule without any seed. The transmission of as-grown crystal is up to 70% in the UV-VIS-NIR region and is with an intense characteristic absorption of Cr2+ near 1770 nm. The X-ray photoelectron spectroscopy (XPS) shows that the incorporation of chlorine anions does not significantly affect the valence distribution of components in the crystal. The mid-infrared photoluminescence spectra show a strong and broad emission band centered at 2400 nm with a width of 600 nm under the 1770 nm laser excitation at room temperature. The calculated cross sections of absorption and emission were 1.31×10−18 and 1.4×10−18 cm2, respectively. The measured photoluminescence decay time was about 6.9 μs at room temperature. It is confirmed that the method of CVT with NH4Cl is suitable for the growth of Cr2+:ZnSe single crystals, which are expected to have a promising prospect in mid-infrared laser applications in further.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.