The electroforming and resistive switching behaviors in the Ag/TaOx/Pt trilayer structure are investigated under a continual change of temperatures between 300 K and 100 K to distinguish the contributions of Ag ions and oxygen vacancies in developing of conducting filaments. For either electroforming or resistive switching, a significantly higher forming/set voltages is needed as the device is operated at 100 K, as compared to that observed when operating at 300 K. The disparity in forming/set voltages of Ag/TaOx/Pt operating at 300 K and 100 K is attributed to the contribution of oxygen vacancies, in addition to Ag atoms, in formation of conducting filament at 100 K since the mobilities of oxygen vacancies and Ag ions become comparable at low temperature. The presence of oxygen vacancy segment in the conducting filament also modifies the reset current from a gradually descending behavior (at 300 K) to a sharp drop (at 100 K). Furthermore, the characteristic set voltage and reset current are irreversible as the operation temperature is brought from 100 K back to 300 K, indicating the critical role of filament constituents on the switching behaviors of Ag/oxide/Pt system.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.