The Auger recombination coefficient in quasi-bulk InxGa1−xN (x∼9%–15%) layers grown on GaN (0001) is measured by a photoluminescence technique. The samples vary in InN composition, thickness, and threading dislocation density. Throughout this sample set, the measured Auger coefficient ranges from 1.4×10−30to2.0×10−30cm6s−1. The authors argue that an Auger coefficient of this magnitude, combined with the high carrier densities reached in blue and green InGaN∕GaN (0001) quantum well light-emitting diodes (LEDs), is the reason why the maximum external quantum efficiency in these devices is observed at very low current densities. Thus, Auger recombination is the primary nonradiative path for carriers at typical LED operating currents and is the reason behind the drop in efficiency with increasing current even under room-temperature (short-pulsed, low-duty-factor) injection conditions.
Auger recombination is determined to be the limiting factor for quantum efficiency for InGaN–GaN (0001) light-emitting diodes (LEDs) at high current density. High-power double-heterostructure (DH) LEDs are grown by metal-organic chemical vapor deposition. By increasing the active layer thickness, DH LEDs can reach a maximum in quantum efficiency at current densities above 200A∕cm2. Encapsulated thin-film flip-chip DH LEDs with peak wavelength of 432nm have an external quantum efficiency of 40% and output power of 2.3W at 2A.
Data are presented on high-power AlGaInN flip-chip light-emitting diodes (FCLEDs). The FCLED is “flipped-over” or inverted compared to conventional AlGaInN light-emitting diodes (LEDs), and light is extracted through the transparent sapphire substrate. This avoids light absorption from the semitransparent metal contact in conventional epitaxial-up designs. The power FCLED has a large emitting area (∼0.70 mm2) and an optimized contacting scheme allowing high current (200–1000 mA, J∼30–143 A/cm2) operation with low forward voltages (∼2.8 V at 200 mA), and therefore higher power conversion (“wall-plug”) efficiencies. The improved extraction efficiency of the FCLED provides 1.6 times more light compared to top-emitting power LEDs and ten times more light than conventional small-area (∼0.07 mm2) LEDs. FCLEDs in the blue wavelength regime (∼435 nm peak) exhibit ∼21% external quantum efficiency and ∼20% wall-plug efficiency at 200 mA and with record light output powers of 400 mW at 1.0 A.
Optical cavity effects have a significant influence on the extraction efficiency of InGaN/GaN quantum-well-heterostructure flip-chip light-emitting diodes (FCLEDs). Light emitted from the quantum well (QW) self-interferes due to reflection from a closely placed reflective metallic mirror. The interference patterns couple into the escape cone for light extraction from the FCLED. This effect causes significant changes in the extraction efficiency as the distance between the QW and the metallic mirror varies. In addition, the radiative lifetime of the QW also changes as a function of the distance between the QW and the mirror surface. Experimental results from packaged FCLEDs, supported by optical modeling, show that a QW placed at an optimum distance from the mirror provides a ∼2.3× increase in total light output as compared to a QW placed at a neighboring position corresponding to a minimum in overall light extraction.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.