The effect of radiation-induced disordering in a nuclear reactor (fast neutrons fluence Φ = 5 · 10 19 cm 2 , Tirr = 340 K) on resistivity ρ, superconducting transition temperature TC and upper critical field HC 2 of polycrystalline MgCNi3 samples was investigated. It was found that TC decreases under irradiation from 6.5 to 2.9 K and completely recovers after annealing at 600 • C. Temperature dependences ρ(T ) are characteristic of compounds with strong electron-phonon interaction. The dHC 2 /dT behaviour testifies to a considerable decrease in density of electronic state at Fermi level N (EF ) in the course of disordering.Radiation-induced disordering caused by irradiation with high-energy particles is a unique method of investigating the properties of superconducting and normal states of ordered crystals [1,2]. Even in broad-band metals, such as intermetallic compounds with A15 structure, long-range ordering loss leads to considerable rearrangement of the electronic spectrum, resulting in disappearance of individual features of the electronic structure. Disordering causes decrease in densities at Fermi level N (E F ) and respective noticeable drop of T C in compounds with high initial N (E F ) (Nb 3 Sn or V 3 Si), and considerable (from 1.5 to 7 K) rise of T C in compounds with low N (E F ) and T C due to growth of N (E F ) (Mo 3 Si and Mo 3 Ge) [3,4,5]. In type HTSC compounds, disordering leads to more significant changes in properties: fast and complete T C degradation is accompanied with N (E F ) decrease and metal-insulator transition [2]. Thus investigation of response of a system to radiation-induced disordering serves as a kind of a test to reveal the characteristic features of its electron states. It was shown in recent papers [6,7] that T C drop from 38 to 5 K observed at MgB 2 under radiation-induced disordering is connected mainly with considerable drop of N (E F ), similar to Nb 3 Sn or V 3 Si compounds. In our investigation, we concentrated on the effect of disordering on the properties of superconducting compound MgCNi 3 (T C ∼ 8 K) with perovskite cubic structure of type SrTiO 3 , unconventional for intermetallides [8]. Our interest in this system was explained by the fact that its ground state is close to ferromagnetic due to the presence of a narrow peak in N (E) located 45 meV below the Fermi level [9]. This allowed us to regard it as a candidate for an unconventional (possibly triplet) superconductivity, similar to Sr 2 RuO 4 compound. It is known that in Sr 2 RuO 4 , as distinct from conventional superconducting compounds (intermetallides), T C undergoes anomalously strong suppression even under a slight disorder [10]. In MgCNi 3 , maximum T C is achieved at excess of carbon content only (nominal composition MgC 1.5 Ni 3 ), even though, according to neutron diffraction study, the actual composition is closer to Mg 0.96 CNi 3 , and excess carbon occupies the region between sample grain boundaries [11].In the sample preparation, fine powders Mg, C and Ni with purity better than 99.5% were used...

No abstract

No abstract

No abstract

No abstract