The fibre laser has been receiving great attention due to its advantages of high efficiency, high power and high beam quality, and is expected to be one of the most desirable heat sources for high-speed and deep-penetration welding. In this study, therefore, in bead-on-plate welding of Type 304 stainless steel plates with 6 kW fibre laser, the effects of laser power, power density and welding speed on the formation of sound welds were investigated with four laser beams of 130, 200, 360 and 560 µm in spot diameter, and their welding phenomena were clarified with high-speed video cameras and an x-ray transmission real-time imaging system. The weld beads showed a keyhole type of penetration at any diameter, and the maximum penetration of 11 mm in depth was obtained at 130 µm spot diameter and 0.6 m min−1 welding speed. It was found that the laser power density exerted a remarkable effect on the increase in weld penetration at higher welding speeds, and sound partially penetrated welds without welding defects such as porosity, underfilling or humping could be produced at wide process windows of welding speeds between 4.5 and 10 m min−1 with fibre laser beams of 360 µm or 560 µm in spot diameter. The high-speed video observation pictures and the x-ray images of the welding phenomena at 6 m min−1 welding speed and 360 µm spot diameter show that a sound weld bead was formed owing to a long molten pool suppressing and accommodating spattering and a stable keyhole generating no bubbles from the tip, respectively.
The objectives of this research are to investigate penetration characteristics, to clarify welding phenomena and to develop high quality welding procedures in bead on plate welding of type 304 austenitic stainless steel plates with a 10 kW fibre laser beam. The penetration depth reached 18 mm at the maximum at 5 mm s 21 . At 50 mm s 21 or lower welding speeds, however, porosity was generated at any fibre laser spot diameter. On the other hand, at 100 mm s 21 or higher welding speeds, underfilling and humping weld beads were formed under the conventionally and tightly focused conditions respectively. The generation of spatters was influenced mainly by a strong shear force of a laser induced plume and was greatly reduced by controlling direction of the plume blowing out of a keyhole inlet. The humping formation was dependent upon several dynamic or static factors, such as melt volume above the surface, strong melt flow to the rear molten pool on the top surface, solidification rate and narrow molten pool width and corresponding high surface tension. Its suppression was effective by producing a wider weld bead width under the defocused laser beam conditions or reduction of melt volume out of keyhole inlet under the full penetration welding conditions. Concerning porosity, X-ray transmission in situ observation images demonstrated that pores were formed not only from the tip of the keyhole but also at the middle part because of high power density. The keyhole behaviour was stabilised using a nitrogen shielding gas, resulting in porosity prevention. Consequently, to produce high quality welds in 10 kW high power fibre laser welding, the reduction procedures of welding defects were required on the basis of understanding their formation mechanism, and 10 kW fibre laser power could produce sound deeply penetrated welds of 18 mm depth in a nitrogen shielding gas.
Conventional fusion welding of aluminium and copper dissimilar materials is difficult because of poor weldability arising from the formation of brittle intermetallic compounds on the weld zone as well as different chemical, mechanical and thermal properties of welded joints. Joining of Al and Cu plates or sheets offers a metallurgical challenge due to unavoidable formation of brittle intermetallic compounds. Therefore, it is necessary to effectively suppress the formation and growth of Al-Cu intermetallic compounds. For welding of dissimilar Al and Cu sheets, no systematic work has been conducted to reduce these defects. Thus, this paper focuses on the effect of welding speed on the quality of a lap weld joint in the Al and Cu sheets with a single mode fibre laser. It was found that consequently sound strong weld joints could be produced by suppressing the formation of intermetallic compounds in the interface zone at extremely high speeds.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.