Polyamide reverse osmosis (RO) membranes with carbon nanotubes (CNTs) are prepared by interfacial polymerization using trimesoyl chloride (TMC) solutions in n-hexane and aqueous solutions of m-phenylenediamine (MPD) containing functionalized CNTs. The functionalized CNTs are prepared by the reactions of pristine CNTs with acid mixture (sulfuric acid and nitric acid of 3:1 volume ratio) by varying amounts of acid, reaction temperature, and reaction time. CNTs prepared by an optimized reaction condition are found to be well-dispersed in the polyamide layer, which is confirmed from atomic force microscopy, scanning electron microscopy, and Raman spectroscopy studies. The polyamide RO membranes containing well-dispersed CNTs exhibit larger water flux values than polyamide membrane prepared without any CNTs, although the salt rejection values of these membranes are close. Furthermore, the durability and chemical resistance against NaCl solutions of the membranes containing CNTs are found to be improved compared with those of the membrane without CNTs. The high membrane performance (high water flux and salt rejection) and the improved stability of the polyamide membranes containing CNTs are ascribed to the hydrophobic nanochannels of CNTs and well-dispersed states in the polyamide layers formed through the interactions between CNTs and polyamide in the active layers.
Various forms of carbon nanotubes have been utilized in water treatment applications. The unique characteristics of carbon nanotubes, however, have not been fully exploited for such applications. Here we exploit the characteristics and corresponding attributes of carbon nanotubes to develop a millimetre-thick ultrafiltration membrane that can provide a water permeability that approaches 30,000 l m À 2 h À 1 bar À 1 , compared with the best water permeability of 2,400 l m À 2 h À 1 bar À 1 reported for carbon nanotube membranes. The developed membrane consists only of vertically aligned carbon nanotube walls that provide 6-nm-wide inner pores and 7-nm-wide outer pores that form between the walls of the carbon nanotubes when the carbon nanotube forest is densified. The experimental results reveal that the permeance increases as the pore size decreases. The carbon nanotube walls of the membrane are observed to impede bacterial adhesion and resist biofilm formation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.