Two-dimensional (2-D) metal chalcogenides have received great attention because of their unique properties, which are different from bulk materials. A challenge in implementing 2-D metal chalcogenides in emerging devices is to prepare a well-crystallized layer over large areas at temperatures compatible with current fabrication processes. Tin monosulfide, a p-type layered semiconductor with a high hole mobility, is a promising candidate for realizing large-area growth at low temperatures because of its low melting point. However, tin sulfides exist in two notable crystalline phases, SnS and SnS2. Therefore, it is imperative to control the oxidation state of Sn to achieve a pure SnS film. Here, the synthesis of SnS thin films by atomic-layer-deposition (ALD) is demonstrated using bis(1-dimethylamino-2-methyl-2-propoxy)tin(II) and H2S as Sn and S sources, respectively, over a wide temperature window (90–240 °C). Impurities such as carbon, oxygen, and nitrogen were negligibly detected. The morphological evolution of plate-like orthorhombic SnS grains was observed above 210 °C. Moreover, properties of thin film transistors and gas sensors using SnS films as the active layers were investigated. The SnS ALD process would provide promising opportunities to exploit the intriguing properties of the 2-D metal chalcogenides for realizing emerging electronic devices.
The utilization of p-p isotype heterojunctions is an effective strategy to enhance the gas sensing properties of metal-oxide semiconductors, but most previous studies focused on p-n heterojunctions owing to their simple mechanism of formation of depletion layers. However, a proper choice of isotype semiconductors with appropriate energy bands can also contribute to the enhancement of the gas sensing performance. Herein, we report nickel oxide (NiO)-decorated cobalt oxide (CoO) nanorods (NRs) fabricated using the multiple-step glancing angle deposition method. The effective decoration of NiO on the entire surface of CoO NRs enabled the formation of numerous p-p heterojunctions, and they exhibited a 16.78 times higher gas response to 50 ppm of CH at 350 °C compared to that of bare CoO NRs with the calculated detection limit of approximately 13.91 ppb. Apart from the p-p heterojunctions, increased active sites owing to the changes in the orientation of the exposed lattice surface and the catalytic effects of NiO also contributed to the enhanced gas sensing properties. The advantages of p-p heterojunctions for gas sensing applications demonstrated in this work will provide a new perspective of heterostructured metal-oxide nanostructures for sensitive and selective gas sensing.
The utilization of edge sites in two-dimensional materials including transition-metal dichalcogenides (TMDs) is an effective strategy to realize high-performance gas sensors because of their high catalytic activity. Herein, we demonstrate a facile strategy to synthesize the numerous edge sites of vertically aligned MoS and larger surface area via SiO nanorod (NRs) platforms for highly sensitive NO gas sensor. The SiO NRs encapsulated by MoS film with numerous edge sites and partially vertical-aligned regions synthesized using simple thermolysis process of [(NH)MoS]. Especially, the vertically aligned MoS prepared on 500 nm thick SiO NRs (500MoS) shows approximately 90 times higher gas-sensing response to 50 ppm NO at room temperature than the MoS film prepared on flat SiO, and the theoretical detection limit is as low as ∼2.3 ppb. Additionally, it shows reliable operation with reversible response to NO gas without degradation at an operating temperature of 100 °C. The use of the proposed facile approach to synthesize vertically aligned TMDs using nanostructured platform can be extended for various TMD-based devices including sensors, water splitting catalysts, and batteries.
In order to develop high performance chemoresistive gas sensors for Internet of Everything applications, low power consumption should be achieved due to the limited battery capacity of portable devices. One of the most efficient ways to reduce power consumption is to lower the operating temperature to room temperature. Herein, we report superior gas sensing properties of SnS2 nanograins on SiO2 nanorods toward NO2 at room temperature. The gas response is as high as 701% for 10 ppm of NO2 with excellent recovery characteristics and the theoretical detection limit is evaluated to be 408.9 ppb at room temperature, which has not been reported for SnS2-based gas sensors to the best of our knowledge. The SnS2 nanograins on the template used in this study have excessive sulfur component (Sn:S = 1:2.33) and exhibit p-type conduction behavior. These results will provide a new perspective of nanostructured two-dimensional materials for gas sensor applications on demand.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.