The recovery of Zr from Zircaloy-4 (Zry-4) cladding hulls using a chlorination method was demonstrated for complete conversion of Zr into ZrCl 4 . A chlorination reaction was performed by reacting Zry-4 hulls for 8 h under a 70 cc/min Cl 2 + 70 cc/min Ar flow at 380 o C. The initial weight of the reactant (51.7 g) decreased to 0.49 g after 8 h of operation, which is only 0.95wt% of the initial weight. The weight of the total reaction products was 121.7 g with a high Zr purity of 99.80wt%. Fe and Sn were identified as major (0.18wt%) and minor (0.02wt%) impurities of the reaction products, respectively. It was also shown that Zr exhibited a high recovery ratio of 96.95wt% with a relatively small experimental loss of 2.34wt%. Observation of the reaction residues revealed that the chlorination reaction was dominant along the longitudinal direction, and surface oxide layers remained as reaction residues. The high purity and recovery ratio of Zr proposed the feasibility of the chlorination technique as an effective hull waste treatment method.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.