A novel polyethoxysilsesquiazane ([EtOSi(NH)1.5]n, EtOSZ) was synthesized by ammonolysis at −78 °C of ethoxytrichlorosilane (EtOSiCl3), which was isolated by distillation as a reaction product of SiCl4 and EtOH. Attenuated total reflection-infra red (ATR-IR), 13C-, and 29Si-nuclear magnetic resonance (NMR) spectroscopic analyses of the ammonolysis product resulted in the detection of Si–NH–Si linkage and EtO group. The simultaneous thermogravimetric and mass spectrometry analyses of the EtOSZ under helium revealed cleavage of oxygen-carbon bond of the EtO group to evolve ethylene as a main gaseous species formed in-situ, which lead to the formation at 800 °C of quaternary amorphous Si–C–N with an extremely low carbon content (1.1 wt %) when compared to the theoretical EtOSZ (25.1 wt %). Subsequent heat treatment up to 1400 °C in N2 lead to the formation of X-ray amorphous ternary Si–O–N. Further heating to 1600 °C in N2 promoted crystallization and phase partitioning to afford Si2N2O nanocrystallites identified by the XRD and TEM analyses. The thermal stability up to 1400 °C of the amorphous state achieved for the ternary Si-O-N was further studied by chemical composition analysis, as well as X-ray photoelectron spectroscopy (XPS) and 29Si-NMR spectroscopic analyses, and the results were discussed aiming to develop a novel polymeric precursor for ternary amorphous Si–O–N ceramics with an enhanced thermal stability.
Silsesquioxane (SQ) derivatives possessing intramolecular H2C = CH- groups and Si-H groups were designed as precursors for ternary silicon oxycarbide (SiOC). By using R-Si(OMe)3, H-Si(OEt)3 and (H-Si(Me)2)2O as starting compounds, SQ derivatives of VH-SQ (R = vinyl) and St-H-SQ (R = stylyl) were successfully synthesized through the conventional sol-gel route. Simultaneous thermogravimetric and mass spectroscopic analyses up to 1000 °C revealed that in situ cross-linking via hydrosilylation and demethanation of VH-SQ suppressed the evolution of gaseous hydrocarbon species to afford amorphous SiOC having a composition close to the desired stoichiometric SiO2(1−x)Cx (x = ca. 0.3) with a high yield. The effect of carbon content on the phase separation and crystallization of the SQ-derived amorphous SiOC was studied by several spectroscopic analyses and TEM observation. The results were discussed aiming to develop a novel polymer-derived ceramics (PDCs) route for in situ formation of binary β-SiC-amorphous SiO2 nanocomposites with enhanced thermal and mechanical stability.
Polyalkoxysilsesquiazanes ([ROSi(NH)1.5]n, ROSZ, R = Et, nPr, iPr, nBu, sBu, nHex, sHex, cHex, decahydronaphthyl (DHNp)) were synthesized by ammonolysis at −78 °C of alkoxytrichlorosilane (ROSiCl3), which was isolated by distillation as a reaction product of SiCl4 and ROH. The simultaneous thermogravimetric and mass spectrometry analyses of the ROSZs under helium revealed a common decomposition reaction, the cleavage of the oxygen–carbon bond of the RO group to evolve alkene as a main gaseous species formed in-situ, leading to the formation of microporous amorphous Si–O–N at 550 °C to 800 °C. The microporosity in terms of the peak of the pore size distribution curve located within the micropore size range (<2 nm) and the total micropore volume, as well as the specific surface area (SSA) of the Si–O–N, increased consistently with the molecular size estimated for the alkene formed in-situ during the pyrolysis. The CO2 capture capacity at 0 °C of the Si–O–N material increased consistently with its SSA, and an excellent CO2 capture capacity of 3.9 mmol·g−1 at 0 °C and CO2 1 atm was achieved for the Si–O–N derived from DHNpOSZ having an SSA of 750 m2·g−1. The CO2 capture properties were further discussed based on their temperature dependency, and a surface functional group of the Si–O–N formed in-situ during the polymer/ceramics thermal conversion.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.