Composite resin becomes an essential material in pediatric dentistry. However, incremental filling of composite resin to minimize the polymerization shrinkage takes time. To reduce the polymerization shrinkage, clinicians and researchers have focused on bulk-filling materials. Bulk-base composite resin is newly introduced as bulk-filling composite resin. The purpose of this study was to evaluate microhardness profile of bulk-base composite resin according to the depth of cure. A high flow bulk-base material and a low flow bulk-base material were used for experimental group, and a conventional composite resin was used for control group. Each group consist of 20 specimens, 3.5 × 3.5 × 5.0 mm mold was used to make specimen. Specimens were sectioned at the 2 mm and the 3 mm depth with milling machine. Microhardness profile was measured at the surface, 2 mm depth, 3 mm depth, and 4 mm depth. Microhardness of control group showed statistically significant difference (p < 0.05) according to the polymerization depth. In contrast, experimental group showed no statistically significant difference, except between 0 mm and 4 mm at HFB, 0 mm and 2 mm, 0 mm and 3 mm at MFB. At the surface and the 2 mm depth, the control group showed higher microhardness than the experimental groups (p < 0.05). However, at the 4 mm depth, the experimental groups showed significantly higher microhardness (p < 0.05). The results from this study, the bulk-base composite resin showed higher microhardness at the 4 mm and lower microhardness at the surface and the 2 mm depth. Therefore, if bulk-base resin overcomes the mechanical weakness, it could be considered using in pediatric dentistry.
The purpose of this study is to analyze the cariogenicity of vitamin supplements for children by the Caries Potentiality Index (CPI), pH drop capacity, proliferation rate of Streptococcus mutans. Four vitamin supplements were selected-Noma (NM), Cenovis Kids (CK), Animal Parade (AP), and Character Vitamin (CV). CPI value decreased in the order of AP, CV, CK, and NM. Initial values of all experimental groups showed acidity below pH 7.0. Analysis of the colony forming units of Streptococcus mutans showed that NM and CV resulted a higher proliferation rate (p < 0.05) than CK and AP (p < 0.05). Bacterial activity of the control group was lower than other groups when observed with a confocal laser scanning microscope. Considering the bacterial activity and acidity of vitamin supplements, it is necessary to pay close attention when children taken the vitamin supplements for their oral health.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.