This paper presents the effects of matrix and interface on the fracture toughness and progressive damage mechanisms of 2.5D woven SiCf/SiC composites. Third-generation SiC fibers were selected. 2.5D woven SiCf/SiC composites with four interfacial layers PyC, PyC/SiC, BN, BN/SiC and two matrix polycarbosilane (PCS) and liquid hyperbranched polycarbosilane with vinyl groups (VHPCS) were prepared by a combination of chemical vapour deposition (CVD), chemical vapor infiltration (CVI), and precursor infiltration pyrolysis (PIP) processes, respectively. Single edge notch bending (SENB) tests were carried out to investigate the fracture toughness. Moreover, acoustic emission (AE) and X-ray micro-computed tomography (Micro-CT) techniques were employed to analyze the progressive mechanical properties and failure mechanism. Results showed that the matrix and interface have significant effects on the fracture toughness. Moreover, 2.5D woven composites with PyC/SiC interfacial layers and VHPCS matrix have the highest fracture toughness (16.93 ± 1.20 Mpa • m1/2). Furthermore, during progressive damage, the pores can influence the crack expansion path, and effectively regulate the stress concentration and increase the toughness of the composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.