high energy and power density, long cycle life, low cost, and environmental benignity. [3] Due to the high capacity of the currently used graphite anode −372 mAh g-1 , [1b,4] commercial cathodes have become the bottleneck for improving the energy density. [5] In addition, cathode materials take up about 40% of the total material cost of typical LIB cells. It is therefore crucial to develop cathode materials with high energy density and low cost, while maintaining superior safety features. [6] Driven by the wide deployment of electric vehicles in recent years, the demand for safer cathode materials with higher capacity and lower cost has become imperative. [2b] The specific capacity depends on the inherent physical properties of the cathode materials. Commercial materials such as LiCoO 2 , Li(Ni x Mn y Co z)O 2 , Li(Ni x Co y Al z)O 2 , LiMn 2 O 4 and LiFePO 4 all possess discharge capacities below 200 mAh g-1. [7] Ni-rich NCM, NCA, and Li-rich oxides are all prospective cathodes for high-energy LIBs as they can exhibit high specific discharge capacities above 200 mAh g-1. [6c] As compared with Ni-rich NCM and NCA, Li-rich Mn-based layered oxide (LMLO) cathode materials are cheaper and have higher specific capacity. They can deliver an initial specific discharge capacity that approaches 300 mAh g-1 , nearly doubling the capacity of commercially used cathodes and close to the limit for lithiated transition metal oxides. [8] Figure 1 lists the main development milestones of LMLO. In 1997 a novel material, LiCoO 2-Li 2 MnO 3 , was found by Numata et al., [9] a discovery that initiated intensive work on high energy density cathode materials. This group studied these materials intensively and demonstrated their cycling stability in the range of 3.0-4.3 V versus Li. [10] In 1999, Kalyani et al. reported that Li 2 MnO 3 can undergo electrochemical activation at potentials >4.5 V versus Li. [11] Dahn et al. described the charge compensation mechanism of LMLO, [12] and these cathodes were shown to provide high capacity at high operational voltage (>4.5 V). [13] In 2004, Thackeray et al. explored xLi 2 M′O 3-(1-x)LiMn 0.5 Ni 0.5 O 2 cathode materials with M′ = Zn, Ti, or Mn, concluding that Li 2 M′O 3 and LiMn 0.5 Ni 0.5 O 2 in these composite materials were integrated by short-range interactions. [14] The following Rechargeable lithium-ion batteries have become the dominant power sources for portable electronic devices, and are regarded as the battery technology of choice for electric vehicles and as potential candidates for grid-scale storage. Commercial lithium-ion batteries, after three decades of cell engineering, are approaching their energy density limits. Toward continually improving the energy density and reducing cost, Li-rich Mn-based layered oxide (LMLO) cathodes are receiving more and more attention due to their high discharge capacity and low cost. However, commercialization has been hampered by severe capacity and voltage decay, sluggish rate capability, and poor safety performance during charge/discharge cyc...

No abstract

Single-crystalline cathodes are the most promising candidates for highenergy-density lithium-ion batteries (LIBs). Compared to their polycrystalline counterparts, single-crystalline cathodes have advantages over liquid-electrolyte-based LIBs in terms of cycle life, structural stability, thermal stability, safety, and storage but also have a potential application in solid-state LIBs. In this review, the development history and recent progress of single-crystalline cathodes are reviewed, focusing on properties, synthesis, challenges, solutions, and characterization. Synthesis of single-crystalline cathodes usually involves preparing precursors and subsequent calcination, which are summarized in the details. In the following sections, the development issues of single-crystalline cathodes, including kinetic limitations, interfacial side reactions, safety issues, reversible planar gliding and micro-cracking, and particle size distribution and agglomeration, are systematically analyzed, followed by current solutions and characterization techniques. Finally, this review is concluded with proposed research thrusts for the future development of singlecrystalline cathodes.

No abstract

No abstract

No abstract

Li-rich Mn-based layered oxide cathodes with a high discharge capacity hold great promise for high energy density lithium-ion batteries. However, application is hampered by voltage and capacity decay and gas evolution during cycling due to interfacial side reactions. Here, we report coating by oxygen-deficient perovskite La 0.9 Sr 0.1 CoO 3 using the Pechini process. X-ray photoelectron spectroscopy and scanning transmission electron microscopy both exhibit a uniform coating layer with a high oxygen vacancy concentration. The coating effectively mitigates the first cycle irreversible capacity loss and voltage decay while increasing cyclability. Optimized coating improves capacity retention from 55.6% to 84.8% after 400 cycles at 2 C. Operando differential electrochemical mass spectroscopy shows that such a coating can significantly mitigate the release of oxygen and carbon dioxide. Electrochemical impedance spectroscopy and post-mortem analysis indicate that the coating layer forms a stable interface and restricts structure evolution and cation mixing during cycling, conferring these cathode materials with better cycling and voltage stability. The perovskite can be applied to other cathodes with high voltage and capacity to suppress interfacial side reactions toward developing stable high energy density batteries.

No abstract