In the scientific industry, sustainable nanotechnology has attracted great attention and has been successful in facilitating solutions to challenges presented in various fields. For the present work, silver nanoparticles (AgNPs) were prepared using a chemical reduction synthesis method. Then, a low-temperature sintering process was deployed to obtain an Ag-conductive ink preparation which could be applied to a flexible substrate. The size and shape of the AgNPs were characterized by ultraviolet–visible spectrophotometry (UV-Vis) and transmission electron microscopy (TEM). The experiments indicated that the size and agglomeration of the AgNPs could be well controlled by varying the reaction time, reaction temperature, and pH value. The rate of nanoparticle generation was the highest when the reaction temperature was 100 °C within the 40 min reaction time, achieving the most satisfactorily dispersed nanoparticles and nanoballs with an average size of 60.25 nm at a pH value of 8. Moreover, the electrical resistivity of the obtained Ag-conductive ink is controllable, under the optimal sintering temperature and time (85 °C for 5 min), leading to an optimal electrical resistivity of 9.9 × 10−6 Ω cm. The results obtained in this study, considering AgNPs and Ag-conductive ink, may also be extended to other metals in future research.
Noble metal nanoparticles have special properties in optical, electronic, and physical chemistry due to their high surface area and volume. With the development of electronic printing technology, inkjet printing has gradually replaced traditional spin coating and blade coating, since it leads to more material savings and a faster batch production, and the pattern can be easily designed by a computer. In this study, Ag nanoparticles were prepared by a chemical reduction method. Non-toxic, environment-friendly agents were selected to fabricate a single-shape, uniform-size, crystal-form, and monodisperse product. The effects of the reducing agent ratio and the stabilizer ratio on the size, shape, and stability of the nanoparticles are discussed. The silver nanoparticles were characterized by an ultraviolet-visible spectrophotometer (UV-vis) and a transmission electron microscope (TEM). In addition, in order to prepare conductive ink that can stably disperse for a long time and that can be applied to inkjet printing on a PET flexible substrate at a lower sintering temperature, a sintering agent and a commercial surfactant were added. The experimental results show that the best addition ratio of the precursor to the reducing agent and the stabilizer is 1:6:1. The conductive silver ink was printed and treated by a70 mM NaCl solution, and the electric resistivity was 5.17×10−4 Ω· cm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.