Monodisperse carbon nanodots (MCNDs) having an identical composition, structure, shape and size possess identical chemical and physical properties, making them highly promising for various technical and medical applications. Herein, we report a facile and effective route to obtain monodisperse carbon nanodots 3.5 ± 0.9 nm in size by thermal decomposition of organosilane within the pores of monodisperse mesoporous silica particles with subsequent removal of the silica template. Structural studies demonstrated that the MCNDs we synthesized consist of ∼7-10 defective graphene layers that are misoriented with respect to each other and contain various oxygen-containing functional groups. It was demonstrated that, owing to their identical size and chemical composition, the MCNDs are formed via coagulation primary aggregates ∼10-30 nm in size, which are, in turn, combined into secondary porous spherical aggregates ∼100-200 nm in diameter. The processes of coagulation of MCNDs and peptization of their hierarchical aggregates are fully reversible and can be controlled by varying the MCND concentration or the pH value of the hydrosols. Submicrometer spherical aggregates of MCNDs are not disintegrated as the hydrosol is dried. The thus obtained porous spherical aggregates of MCNDs are promising for drug delivery as a self-disassembling container for medicinal preparations.
Photo-thermo-refractive (PTR) glasses are the class of polyfunctional materials that combine the properties of several monofunctional materials such as photo-refractive, laser, luminescent, and plasmonic ones. Based on PTR glasses, various diffractive holographic elements and photonic devices were developed in both the volume and fiber versions. In this paper, the fabrication of optical planar waveguides on PTR glass by low-temperature ion exchange is reported for the first time. Planar waveguides were fabricated through substituting the sodium ions in glass by silver, potassium, rubidium, and cesium ones from the nitrate melts. The silver waveguides were shown to have the largest depth (27 μm) and reveal no birefringence. For the silver waveguides, an increase in the refractive index is caused by differences in the polarizabilities of cations exchanged. The maximum increment of the refractive index was observed in the cesium waveguides (0.0512). An increase in the refractive index and also appearing the birefringence in potassium, rubidium, and cesium waveguides are found to be due to the compressive mechanical stresses and their relaxation. The potentialities of the ion exchange technology for fabricating, in PTR glasses, planar gradient waveguides with low losses (0.5 dB/cm) are demonstrated, the potentialities extending the application field of PTR glasses in photonics.Index Terms-Ion exchange, optical waveguides, photo-thermorefractive glass.
0733-8724
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.