New monolithic multi-layered zirconia restorations are gaining popularity due to their excellent aesthetic properties. However, current knowledge of these newest multi-layer ceramics in terms of mechanical properties is scarce. Three monolithic, multi-layered zirconia materials (Katana, Kuraray Noritake, Japan) were selected for comparison: High Translucent Multi-layered zirconia (HTML), Super Translucent Multi-layered zirconia (STML) and Ultra Translucent Multi-layered zirconia (UTML). Fifteen specimens per group were cut from pre-sintered blocs in each of the four layers (L1, L2, L3, L4) and in different thicknesses (0.4 mm, 0.8 mm and 1.2 mm). Critical fracture load (Fcf) was recorded in 3-point-bending. Flexural strength (σ) in MPa, Vickers hardness (HV) in N/mm2, fracture toughness (KIc) in MPa*m1/2, Weibull Modulus (m) and characteristic Weibull strength (σw) in MPa were assessed. Statistical analysis was performed using ANOVA analysis. FS and KIc were significantly higher (p < 0.05) for Katana™ HTML (652.85 ± 143.76–887.64 ± 118.95/4.25 ± 0.43–5.01 ± 0.81) in comparison to Katana™ STML (280.17 ± 83.41–435.95 ± 73.58/3.06 ± 0.27–3.84 ± 0.47) and UTML (258.25 ± 109.98–331.26 ± 56.86/2.35 ± 0.31–2.94 ± 0.33), with no significant differences between layers and layer thicknesses. The range of indications should be carefully considered when selecting the type of monolithic zirconia for fabrication of dental restorations, as materials widely differ in mechanical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.