Chitosan (CS)/montmorillonite‐K10 (MMTK‐10) clay composite films with different amounts of the clay MMTK‐10 (0.5, 1, 2.5, and 5%) were prepared using a solution‐casting method, and their properties were determined. The objective of this study is to prepare CS/clay nanocomposites and then to investigate the effects of clay content on mechanical, barrier, and thermal properties of these nanocomposites. The prepared films were characterized by Fourier transform infrared spectroscopy, X‐ray diffraction analysis, transmission electron microscopy, and scanning electron microscopy. Barrier properties (oxygen and water permeability), mechanical properties (tensile strength and elongation), and thermal behaviors (thermogravimetric analysis) were investigated and compared. The water vapor and gas permeability values of the composite films decreased significantly with increasing filler concentration. Tensile strength of the composites increased significantly with the addition of clay, and elongation at break decreased with increasing clay concentration. The tensile strength of nanocomposites is up to 34.82 MPa for 5 wt% clay content, and the tensile modulus shows a 74.63% higher value than that of neat CS. The resulting films had an opaque appearance, which depended on the amount of MMTK‐10 added. The oxygen permeability decreased with the increase in MMTK‐10. The minimum oxygen permeability (1.54 cm3/m2 day atm) was recorded for film with 5% MMTK‐10. The water permeability of the composite films decreased significantly between 13 and 22% when clay was added. The dispersed clay improves the thermal stability and enhances the hardness and elastic modulus of the matrix systematically with the increased loading of clay. POLYM. COMPOS., 33:1874–1882, 2012. © 2012 Society of Plastics Engineers
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.