The aim of this study was to develop and evaluate an optimized 3D bioprinting technology in order to fabricate novel scaffolds for the application of endothelial cell repair. Various biocompatible and biodegradable macroporous scaffolds (D = 10 mm) with interconnected pores (D = ~500 µm) were fabricated using a commercially available 3D bioprinter (r3bEL mini, SE3D, USA). The resolution of the printing layers was set at ~100 µm for all scaffolds. Various compositions of polylactic acid (PLA), polyethylene glycol (PEG) and pluronic F127 (F127) formulations were prepared and optimized to develop semi-solid viscous bioinks. Either dimethyloxalylglycine (DMOG) or erythroprotein (EPO) was used as a model drug and loaded in the viscous biocompatible ink formulations with a final concentration of 30% (w/w). The surface analysis of the bioinks via a spectroscopic analysis revealed a homogenous distribution of the forming materials throughout the surface, whereas SEM imaging of the scaffolds showed a smooth surface with homogenous macro-porous texture and precise pore size. The rheological and mechanical analyses showed optimum rheological and mechanical properties of each scaffold. As the drug, DMOG, is a HIF-1 inducer, its release from the scaffolds into PBS solution was measured indirectly using a bioassay for HIF-1α. This showed that the release of DMOG was sustained over 48 h. The release of DMOG was enough to cause a significant increase in HIF-1α levels in the bioassay, and when incubated with rat aortic endothelial cells (RAECs) for 2 h resulted in transcriptional activation of a HIF-1α target gene (VEGF). The optimum time for the increased expression of VEGF gene was approximately 30 min and was a 3-4-fold increase above baseline. This study provides a proof of concept, that a novel bioprinting platform can be exploited to develop biodegradable composite scaffolds for potential clinical applications in endothelial cell repair in cardiovascular disease (CVD), or in other conditions in which endothelial damage occurs.
One of the main applications of bone graft materials is filling the gap after the surgical removal of bone cancer or tumors. Insufficient healing commonly leads to non-union fracture which could lead to cancer resurgence or infection. Emerging 3D printing of on-demand bone graft biomaterials can deliver personalized solutions with minimized risk of relapse and recurrence of cancer after bone removal surgery. This research aims to explore 3D printed calcium phosphate cement (CPC) based scaffolds as novel anti-cancer drug delivery systems to treat bone cancer. For the study, various 3D printed CPC based scaffolds (diameter 5 mm) with interconnected pores were utilized. Various optimized polymeric solutions containing a model anticancer drug 5-fluorouracil (5-FU) was used to homogenously coat the CPC scaffolds. Both hydrophilic Soluplus (SOL) and polyethylene glycol (PEG) and a combination of both were used to develop stable coating solutions. The surface morphology of the coated scaffolds, observed via SEM, revealed deposition of the polymeric solution represented by a semi-smooth surface as opposed to the blank scaffolds that showed a smoother surface. An advanced surface analysis conducted via confocal microscopy showed a homogenous distribution of the drug throughout the coated scaffolds. Solid-state analysis studied by applying differential scanning calorimetry (DSC) and X-ray diffraction (XRD) revealed semi-crystalline nature of the drug whereas mechanical analysis conducted via texture analysis showed no evidence in the change of the mechanical properties of the scaffolds after polymeric solutions were applied. The FTIR analysis revealed no major intermolecular interactions between 5-FU and the polymers used for coatings except for F2 where a potential nominal interaction was evidenced corresponding to higher Soluplus content in the formulation. In vitro dissolution studies showed that almost 100% of the drug released within 2 h for all scaffolds. Moreover, in vitro cell culture using two different cell lines (Hek293T-human kidney immortalized cell line and HeLa-human bone osteosarcoma epithelial cell line) showed significant inhibition of cell growth as a function of decreased numbers of cells after 5 days. It can be claimed that the developed 5-FU coated 3D printed scaffolds can successfully be used as bone graft materials to potentially treat bone cancer or bone neoplasm and for personalized medical solutions in the form of scaffolds for regenerative medicine or tissue engineering applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.