Electron beam processing was considered to be the promising modification method for Al-Mg alloys. An investigation of the effect of high energy density on the surface modification layer was developed. The results demonstrated that the grain boundaries emerged and there are some microcracks formed along grain boundaries due to superfast heating and cooling speed during the treatment process. Due to this special microstructure morphology, the average friction coefficient was decreased but the wear volume was increased, and the yield strength and the ultimate tensile strength are reduced.
Adopting an accurate micro-tensile method based on dynamic mechanical analyzer (DMA) instrument, the tensile strength of three kinds of copper-wire/solder/copper-wire sandwich structured microscale lead-free solder joints that underwent current stressing with a direct current density of 1.0×104 A/cm2 and loading time of 48 hours were investigated, and compared with those solder joints isothermal aged at 100 0C for 48 hours and as-reflowed condition. These three kinds of microscale columnar solder joints have different volumes, i.e., a same diameter of 300 μm but different heights of 100 μm, 200 μm and 300 μm. Experimental results show that both current stressing and isothermal aging degrades the tensile strength of microscale solder joints, and the solder joint with smaller volume obtains higher tensile strength under same test condition. In addition, current stressing induces obvious electromigration (EM) issue under high current density of 1.0×104 A/cm2, resulting in the decreasing of tensile strength and different fracture position, mode and surface morphology of microscale solder joints. The degree of strength degradation increases with the increasing of joint height when keep joint diameter constant, this is mainly due to that electromigration leads to voids form and grow at the interface of cathode, and solder joints with larger volume may contains more soldering defects as well.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.