In air and railway transportation, corrosion and wear lead to the rapid failure of equipment. Epoxy (EP)-based coatings are widely used in research on the anti-corrosion of organic coatings, but their application as materials for wear resistance is limited due to their non-abrasive properties. In this study, a novel high-performance epoxy-based composite coating was developed through the self-assembly of silicon carbide (SiC) and graphene oxide (GO) and the tuning of the interfacial structure with epoxy resin. The coatings were comprehensively characterized, including their electrochemical behavior, a salt spray test, and friction and wear experiments, and the optimal addition ratio of SiC-G@GO (SiC-G@GO was prepared by the self-assembly of γ-(2,3-epoxypropoxy) propytrimethoxysilane (KH560)-modified SiC (SiC-G) on the surface of GO sheets) in the epoxy coatings was explored. Benefiting from the labyrinth effect and their rolling-friction-like microstructure, the 1 wt% SiC-G@GO/EP coating exhibits excellent wear and corrosion resistance. Compared with pure epoxy resin, the 1 wt% SiC-G@GO/EP coating increased by 4 orders of magnitude after 10 days of immersion. The average friction coefficient was 41.5% lower than that of the pure EP coating, and the wear rate was 56.6% lower. This research has positive implications for the development and application of anti-corrosion and wear-resistant organic coatings.
In order to meet the anticorrosion and wear resistance requirements of petroleum pipelines, we selected a polymer (FC) containing difunctional hydroxyl propyl acrylate (HPA) and perfluoroalkyl ethyl acrylate (TEAc-N) free radical polymerization to prepare hydrophobic fluorocarbon chain oil and a hydroxyl special functional group. Combined with tetrafluororesin (F4), the hydrophobic, wear-resistant and corrosion-resistant properties of epoxy coating were improved. The optimum synthesis ratio of TEAc-N:HPA was 9:1, and the FC polymer with the best hydrophobicity was prepared. The hydrophobic angle of the coating was 100.3% higher than that of pure Q235 section steel. By adding 5 wt.% of FC to epoxy resin (EP), the hydrophobicity increased by 65.4% and oleophobicity increased by 32.1% compared with pure EP. The coefficient of friction was reduced by 73.8%. EIS test results showed that the impedance modulus in the low frequency region (|Z|0.01 Hz) was two orders of magnitude higher than that of the pure epoxy coating. The composite coating has sufficient utility to meet the wear, heat and corrosion resistance requirements for oil pipeline transportation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.