The aim of this research was synthesize YBa2Cu3O? (YBCO) and to study the effect of Al2O3 additions at x= 0.00, 0.10, 0.20, 0.50, 1.50 and 3.50 wt.%. The samples were investigated through Thermogravimetric Analyzer (TGA) and X-Ray Diffraction (XRD). All samples prepared by solid state reaction method with calcination process at 900°C and sintering process at 950°C. The TGA analysis indicated weight loss was complete at 910°C. XRD patterns showed the orthorhombic structure with lattice parameters a=3.821 Å, b= 3.880 Å and c= 11.663 Å, respectively. The Al2O3 added samples did not show any new peak however the sharpness and broadening peaks was changed. The crystallite sizes of the samples were calculated from the width of the selected peak and half maximum. The size is slowly increased by increasing the Al2O3 addition. These result indicated that addition does not affect on the structure but the crystallite sizes increase affect the morphology images
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.