This paper reported the enhancement in thermo-mechanical properties and chemical stability of porous SiCOH dielectric thin films fabricated with molecularly scaled pores of uniform size and distribution. The resulting porous dielectric thin films were found to exhibit far stronger resistance to thermo-mechanical instability mechanisms common to conventional SiCOH dielectric thin films without forgoing an ultralow dielectric constant (i.e., ultralow-k). Specifically, the elastic modulus measured by nano-indentation was 13 GPa, which was substantially higher than the value of 6 GPa for a porous low-k film deposited by a conventional method, while dielectric constant exhibited an identical value of 2.1. They also showed excellent resistance against viscoplastic deformation, as measured by the ball indentation method, which represented the degree of chemical degradation of the internal bonds. Indentation depth was measured at 5 nm after a 4-h indentation test at 400 °C, which indicated an ~89% decrease compared with conventional SiCOH film. Evolution of film shrinkage and dielectric constant after annealing and plasma exposure were reduced in the low-k film with a self-organized molecular film. Analysis of the film structure via Fourier-transform infrared (FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS) indicated an increase in symmetric linear Si–O–Si molecular chains with terminal –CH3 bonds that were believed to be responsible for both the decrease in dipole moment/dielectric constant and the formation of molecular scaled pores. The observed enhanced mechanical and chemical properties were also attributed to this unique nano-porous structure.
The influence of the dipole polarization of carbon film coatings on their secondary electron emission has been studied. It is shown that plasma fluorination of carbon coatings with low specific surface resistance obtained in microwave plasma of low-pressure ethanol vapor increases the electron work function by 0.6 eV and reduces the secondary electron emission by more than a factor of two. The results can be used to obtain collectors and anti-emission coatings on grid electrodes of high-power electrovacuum devices in the microwave and sub-terahertz ranges. Keywords: microwave plasma, carbon film, plasma fluorination, work function, secondary electron emission.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.