The role of mesoscopic mass transport and re-adsorption effects in electrocatalytic reactions was investigated using the oxygen reduction reaction (ORR) as an example. The electrochemical measurements were performed on structurally well-defined nanostructured model electrodes under controlled transport conditions in a thin-layer flow cell. The electrodes consist of arrays of Pt ultra-microelectrodes (nanodisks) of defined size (diameter approximately 100 nm) separated on a planar glassy carbon (GC) substrate, which were fabricated employing hole-mask colloidal lithography (HCL). The measurements reveal a distinct variation in the ORR selectivity with Pt nanodisk density and with increasing electrolyte flow, showing a pronounced increase of the H2O2 yield, by up to 65%, when increasing the flow rate from 1 to 30 microL s(-1). These results are compared with previous findings and discussed in terms of a reaction model proposed recently (A. Schneider et al., Phys. Chem. Chem. Phys., 2008, 10, 1931), which includes (i) direct reduction to H2O on the Pt surface and (ii) additional H2O2 formation and desorption on both Pt and carbon surfaces and subsequent partial re-adsorption and further reduction of the H2O2 molecules on the Pt surface. The potential of model studies on structurally defined catalyst surfaces and under well-defined mass transport conditions in combination with simulations for the description of electrocatalytic reactions is discussed.
The role of transport and re-adsorption processes on the oxygen reduction reaction (ORR), and in particular on its selectivity was studied using nanostructured model electrodes consisting of arrays of Pt nanostructures of well-defined size and separation on a planar glassy carbon (GC) substrate. The electrochemical measurements were performed under controlled transport conditions in a double-disk electrode thin-layer flow-cell configuration; the model electrodes were fabricated by colloidal lithography techniques, yielding Pt nanostructures of well defined and controlled size and density (diameter: 140 or 85 nm, height: 20 or 10 nm, separation: from 1-2 to more than 10 diameters). The nanostructured model electrodes were characterized by scanning electron microscopy and electrochemical probing of the active surface area (via the hydrogen adsorption charge). The electrocatalytic measurements revealed a pronounced variation of the hydrogen peroxide yield, which increases by up to two orders of magnitude with increasing separation and decreasing size of the Pt nanostructures. Similar, though less pronounced effects were observed upon varying the electrolyte flow and thus the mass transport characteristics. These effects are discussed in a reaction model which includes (i) direct reduction to H(2)O on the Pt surface and (ii) additional H(2)O(2) formation and desorption on both Pt and carbon surfaces and subsequent partial re-adsorption and further reduction of the H(2)O(2) molecules on the Pt surface.
Transport effects in the methanol oxidation reaction (MOR) were investigated using nanostructured Pt/glassy carbon (GC) electrodes and, for comparison, a polycrystalline Pt electrode. The nanostructured Pt/GC electrodes, consisting of a regular array of catalytically active cylindrical Pt nanostructures with 55 +/- 10 nm in diameter and different densities supported on a planar GC substrate, were fabricated employing hole-mask colloidal lithography (HCL). The MOR measurements were performed under controlled transport conditions in a thin-layer flow cell interfaced to a differential electrochemical mass spectrometry (DEMS) setup. The measurements reveal a distinct variation in the MOR activity and selectivity (product distribution) with Pt nanostructure density and with electrolyte flow rate, showing an increasing overall activity, reflected by a higher Faradaic reaction current, as well as a pronounced increase of the turnover frequency for CO(2) formation and of the CO(2) current efficiency with decreasing flow rate and increasing Pt coverage. These findings are discussed in terms of the "desorption-readsorption-reaction" model introduced recently (Seidel et al. Faraday Discuss. 2008, 140, 67). Finally, consequences for applications in direct methanol fuel cells are outlined.
Nanostructured, glassy carbon ͑GC͒ supported Pt/GC electrodes, with Pt nanostructures ͑nanodisks͒ of controlled size ͑100-140 nm in diameter͒ and separation homogeneously distributed on a planar GC substrate, were recently shown to be interesting model systems for electrocatalytic reaction studies ͓M. Gustavsson, H. Fredriksson, B. Kasemo, Z. Jusys, C. Jun, and R. J. Behm, J. Electroanal. Chem., 568, 371 ͑2004͔͒. We present here electron microscopy and electrochemical measurements which reveal that the fabrication of these nanostructured electrodes via colloidal lithography, in addition to the intended nanodisks, results in a dilute layer of much smaller Pt nanoparticles ͑diameter ϳ5 nm͒ on the GC surface in the areas between the Pt nanodisks. We further demonstrate that by using the developed, related method of hole-mask colloidal lithography ͑HCL͒ ͓H. Fredriksson, Y. Alaverdyan, A. Dmitriev, C. Langhammer, D. S. Sutherland, M. Zäch, and B. Kasemo, Adv. Mater. (Weinheim, Ger.), 19, 4297 ͑2007͔͒, similar electrodes can be prepared which are free from these Pt nanoparticles. The effect of the additional small Pt nanoparticles on the electrochemical and electrocatalytic properties of these nanostructured electrodes, which is significant and can become dominant at low densities of the Pt nanodisks, is illustrated and discussed. These results leave HCL the preferred method for the fabrication of nanostructured Pt/GC electrodes, in particular, of low-density Pt/GC electrodes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.