To clarify the feasibility of controlling the refractive index of a polymer by proton beam irradiation, we irradiated 1.0 MeV protons to a fluorinated polyimide film. Before and after the proton irradiation at a fluence between 1×1014 and 7×1016 cm-2, the film surface was scanned by a profilometer. It was found that the depth of a dent, which increases with fluence, was induced by the irradiation. The refractive index of the ion-irradiated region was calculated using the Lorentz–Lorenz equation, substituting the depth of the dent and the projected range of the protons. When the fluorinated polyimide was irradiated at a fluence of 7×1016 cm-2, the refractive index increased by about 3.3%, which agrees with the increment in refractive index measured by spectroscopic ellipsometry. The increment in refractive index (0.21%) induced by the irradiation of protons at the fluence of 1×1015 cm-2 is comparable to the value (0.35%) observed when protons were irradiated to SiO2 glass at a similar fluence. Therefore, it is reasonable to assume that the ion irradiation to a polymer can be a good method for fabricating a high-performance polymer-based optical waveguide.
Space charge formation behavior is compared among crosslinked polyethylene and its two nanocomposites with silica nanofillers with and without surface treatment. By conducting a degassing treatment, we have prepared nine kinds of samples in total. As a result, it was found that the presence of cross-linking by-products suppresses space charge formation. As far as the present silica nanofillers are concerned, their addition to XLPE enhances the formation of negative space charge near the cathode.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.