Tb3+ doped Ba3Gd(PO4)3 and Ba3La(PO4)3 phosphors were synthesized using the traditional high temperature solid state reaction method. The excitation, emission, and decay spectra were measured at room temperature. Efficient energy transfer (ET) from Gd3+ to Tb3+ exists in Tb3+ doped Ba3Gd(PO4)3, and the ET efficiency increases with the increase of Tb3+ concentration. The visible quantum cutting (QC) via cross relaxation was observed upon exciting low-spin (7D(J)) 5d levels of Tb3+ ions. Ba3Tb(PO4)3 sample shows relatively strong emission intensity in comparison with Zn2SiO4: Mn2+ (ZSM) upon 172 nm excitation, and with a decay time τ(1/10) about 6.4 ms under 351 nm excitation, indicating the potential application of this phosphor for plasma display panels (PDPs) and Hg-free lamps.
A "basophilic method" for phenolic hydroxyl bridged lanthanide coordination polymers (CPs) was developed. With this method, eleven CPs with the general formula of [Ln(HL1)L1·H(2)O](n) (Ln = Tb (1), Nd (2), Eu (3), Gd (4), La (5), Er (6), Y (7), H(2)L1 = 4-methyl salicylic acid) and [Ln(HL2)L2·2MeOH](n) (Ln = Eu (8), Tb (9), Gd (10), La (11), H(2)L2 = 3-hydroxy-2-naphthoic acid) were synthesized based on two ligands, and five of them (1-4 and 8) were characterised by X-ray single crystal diffraction. The powder X-ray diffraction patterns (PXRD) of complexes showed that 1-7 are isostructural, 8-11 are isostructural. Furthermore, 1 was characterised by Fourier transform infrared (FT-IR), thermogravimetric analysis (TGA), differential thermal analysis (DTA), elemental analysis (EA), one and two photon luminescence were investigated in detail.
Ce 3þ -doped Ba 3 MgSi 2 O 8 phosphors were prepared by a solid-state reaction route. The photoluminescence properties in the vacuum ultraviolet-vis spectral range and the x ray excited radioluminescence were investigated. Ce 3þ ions were found to enter three different sites in the host lattice. Five excitation bands and two emission bands of Ce (1) 3þ centers were observed in the spectra. For Ce (2) 3þ and Ce (3) 3þ centers, the lowest 5d excitation bands and the emission bands were determined. The light yields of samples under x ray excitation were estimated by comparing the integrated emission intensities of our samples with that of BaF 2 .
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.