The influence of stacking fault energy on plasticity mechanisms in triode-plasma nitrided austenitic stainless steels: implications for the structure and stability of nitrogen-expanded austenite.

Despite much research into steels strengthened through interphase precitation, there remains much that is not clear, such as the role of a range of elements, particularly Mo, in the interphase precipitation process. Four steels were manufactured with identical composition, but with variations in Ti, V, Mo and N content to investigate the effect of composition on interphase precipitation. Alloys were rapidly cooled from the single austenite phase field and isothermally transformed at 630°C and 650°C for 90min. The addition of Mo was found to significantly reduce the austenite to ferrite transformation kinetics, particularly for the V steel. Interphase precipitation was observed in all alloys at both transformation temperatures. For the Ti bearing steel, the two types of precipitate were observed throughout the sample, namely TiC (finer) and Ti2C (coarser), while for the V bearing steels, VC (finer) and V4C3 (coarser) were observed. Where Mo was present in the alloy, it was found dissolved in all carbide types. The (Ti,Mo)C and (V,Mo)C formed by classical planer interphase precipitation (PIP) while the (Ti,Mo)2C and (V,Mo)4C3, that had a much wider row spacing, formed through curved interphase precipitation (CIP). Each adopted one variant of the Baker-Nutting orientation relationship. The Ti-microalloyed steels exhibited the smallest precipitates of all the steels, which were approximately the same size irrespective of whether Mo was present in the alloy and irrespective of the transformation temperature. However, the addition of Mo to the V bearing steels resulted in a significant increase in precipitate volume fraction and a reduction in precipitate size. The mechanisms of interphase precipitation leading to the coincident production of two different precipitate types is considered and the role of Mo on the interphase precipitation process is discussed. The resultant effect on strength is considered.

The entire recrystallisation sequence and associated crystallographic texture evolution of Mg-0.8Zn-0.2Ca (wt.%) alloy was tracked using a quasi-in-situ electron backscatter diffraction (EBSD) method. Characteristic “Rare Earth” (RE) texture was formed, originating mainly from double twins and twinning-related shear bands consisting of compression and double twins. The RE textures appeared during the nucleation stage and were preserved during the relative uniform grain growth period because of solute segregation and concurrent precipitation although the alloying element content was very low. Ca and Zn co-segregated along grain boundaries with no evidence that segregation was preferred along special types of grain boundaries. The interactions between deformation microstructures, concurrent precipitation, solute drag, grain growth and texture evolution are discussed in detail. All the results indicate that Ca performs a similar role to that of RE elements in forming RE texture.

In β titanium alloys, the β stabilizers segregate easily and considerable effort has been devoted to alleviate/eliminate the segregation. In this work, instead of addressing the segregation problems, the segregation was utilized to develop a novel microstructure consisting of a nanometre-grained duplex (α+β) structure and micrometre scale β phase with superior mechanical properties. An as-cast Ti-9Mo-6W alloy exhibited segregation of Mo and W at the tens of micrometre scale. This was subjected to cold rolling and flash annealing at 820 oC for 2 and 5 mins. The solidification segregation of Mo and W leads to a locally different microstructure after cold rolling (i.e., nanostructured β phase in the regions rich in Mo and W and plate-like martensite and β phase in regions relatively poor in Mo and W), which play a decisive role in the formation of the heterogeneous microstructure. Tensile tests showed that this alloy exhibited a superior combination of high yield strength (692 MPa), high tensile strength (1115 MPa), high work hardening rate and large uniform elongation (33.5%). More importantly, the new technique proposed in this work could be potentially applicable to other alloy systems with segregation problems.