Electrospinning of chitosan solutions with poly(ethylene oxide) (PEO) in an aqueous solution of 2 wt% acetic acid was studied. The properties of the chitosan/PEO solutions, including conductivity, surface tension and viscosity, were measured. Morphology of the electrospun chitosan/PEO was observed by using scanning electron micrographs. Results showed that the ultrafine fibers could be generated after addition of PEO in 2:1 or 1:1 mass ratios of chitosan to PEO from 4-6 wt% chitosan/PEO solutions at 15 kV voltage, 20 cm capillary-collector distance and flow rate 0.1 ml/h. During electrospinning of the chitosan/PEO solutions, ultrafine fibers with diameters from 80 nm to 180 nm were obtained, while microfibers with visually thicker diameters could be formed as well. Results of X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and differential scanning calorimeter exhibited the larger electrospun microfibers were almost entirely made from PEO, while the electrospun ultrafine fibers mainly contained chitosan.

No abstract

Graphene is highly desirable as an electromagnetic wave (EM) absorber because of its large interface, high dielectric loss, and low density. Nevertheless, the conductive and electromagnetic parameters of pure graphene are too high to meet the requirement of impedance match, which results in strong reflection and weak absorption. In this paper, we report a facile solvothermal route to synthesize reduced graphene oxide (RGO) nanosheets combined with surface-modified γ-Fe 2 O 3 colloidal nanoparticle clusters. The obtained two-dimensional hybrids exhibit a relatively low EM reflection coefficient (RC) and wide effective absorption bandwidth, which are mainly attributed to the unique microstructure of colloidal nanoparticle clusters assembled on RGO. The nanoparticle clusters have more interfaces. The interfacial polarization within nanoparticle clusters and conductivity loss of RGO plays an important role in absorbing EM power. The minimum RC reaches −59.65 dB at 10.09 GHz with a matching thickness of 2.5 mm. The special integration of some metal oxide semiconductor crystals assembled on RGO sheets provides an effective avenue to design metal oxide semiconductor/carbon hybrids as EM absorbing materials.

Energy storage materials are urgently demanded in modern electric power supply and renewable energy systems. The introduction of inorganic fillers to polymer matrix represents a promising avenue for the development of high energy density storage materials, which combines the high dielectric constant of inorganic fillers with supernal dielectric strength of polymer matrix. However, agglomeration and phase separation of inorganic fillers in the polymer matrix remain the key barriers to promoting the practical applications of the composites for energy storage. Here, we developed a low-cost and environmentally friendly route to modifying BaTiO3 (BT) nanoparticles by a kind of water-soluble hydantoin epoxy resin. The modified BT nanoparticles exhibited homogeneous dispersion in the ferroelectric polymer poly(vinylidene fluoride-co-hexafluoropropylene) (P(VDF-HFP)) matrix and strong interfacial adhesion with the polymer matrix. The dielectric constants of the nanocomposites increased significantly with the increase of the coated BT loading, while the dielectric loss of the nanocomposites was still as low as that of the pure P(VDF-HFP). The energy storage density of the nanocomposites was largely enhanced with the coated BT loading at the same electric field. The nanocomposite with 20 vol % BT exhibited an estimated maximum energy density of 8.13 J cm(-3), which was much higher than that of pure P(VDF-HFP) and other dielectric polymers. The findings of this research could provide a feasible approach to produce high energy density materials for practical application in energy storage.

In this article, the plasma surface modification effects on the chemical, mechanical, and biological properties of electrospun poly (ε-caprolactone) (PCL) random nanofiber meshes (NFMs) were investigated by adjusting plasma chemistry, that is, using glow discharges of N(2) +H(2), NH(3) +O(2), and Ar+O(2) gas mixtures. The surface property changes of electrospun PCL NFMs after those plasma treatments were examined by water contact angle measurements and X-ray photoelectron spectroscopy. The experimental results showed that the plasma treatments introduced polar groups onto the surfaces and thus increased the surface hydrophilicity. From tensile test data, plasma treatment had limited effect on the mechanical properties of PCL random NFMs. The biological properties of the plasma-treated PCL NFMs were examined by cell proliferation assays using mouse osteoblast cells (MC3T3-E1). It was found that the plasma-treated PCL NFMs gave a higher proliferation rate and improved cell adhesion properties as compared with the untreated controls.

No abstract

No abstract

No abstract