This article provides a progress report on the use of galvanic replacement for generating complex hollow nanostructures with tunable and well-controlled properties. We begin with a brief account of the mechanistic understanding of galvanic replacement, specifically focused on its ability to engineer the properties of metal nanostructures in terms of size, composition, structure, shape, and morphology. We then discuss a number of important concepts involved in galvanic replacement, including the facet selectivity involved in the dissolution and deposition of metals, the impacts of alloying and dealloying on the structure and morphology of the final products, and methods for promoting or preventing a galvanic replacement reaction. We also illustrate how the capability of galvanic replacement can be enhanced to fabricate nanomaterials with complex structures and/or compositions by coupling with other processes such as co-reduction and the Kirkendall effect. Finally, we highlight the use of such novel metal nanostructures fabricated via galvanic replacement for applications ranging from catalysis to plasmonics and biomedical research, and conclude with remarks on prospective future directions.

This Perspective provides a contemporary understanding of the shape evolution of colloidal metal nanocrystals under thermodynamically and kinetically controlled conditions. It has been extremely challenging to investigate this subject in the setting of one-pot synthesis because both the type and number of seeds involved would be changed whenever the experimental conditions are altered, making it essentially impossible to draw conclusions when comparing the outcomes of two syntheses conducted under different conditions. Because of the uncertainty about seeds, most of the mechanistic insights reported in literature for one-pot syntheses of metal nanocrystals with different shapes are either incomplete or ambiguous, and some of them might be misleading or even wrong. Recently, with the use of well-defined seeds for such syntheses, it became possible to separate growth from nucleation and therefore investigate the explicit role(s) played by a specific thermodynamic or kinetic parameter in directing the evolution of colloidal metal nanocrystals into a specific shape. Starting from single-crystal seeds enclosed by a mix of {100}, {111}, and {110} facets, for example, one can obtain colloidal nanocrystals with diversified shapes by adjusting various thermodynamic or kinetic parameters. The mechanistic insights learnt from these studies can also be extended to account for the products of conventional one-pot syntheses that involve self-nucleation only. The knowledge can be further applied to many other types of seeds with twin defects or stacking faults, making it an exciting time to design and synthesize colloidal metal nanocrystals with the shapes sought for a variety of fundamental studies and technologically important applications.

Seed-mediated growth is a powerful and versatile approach for the synthesis of colloidal metal nanocrystals. The vast allure of this approach mainly stems from the staggering degree of control one can achieve over the size, shape, composition, and structure of nanocrystals. These parameters not only control the properties of nanocrystals but also determine their relevance to, and performance in, various applications. The ingenuity and artistry inherent to seed-mediated growth offer extensive promise, enhancing a number of existing applications and opening the door to new developments. This Review demonstrates how the diversity of metal nanocrystals can be expanded with endless opportunities by using seeds with well-defined and controllable internal structures in conjunction with a proper combination of capping agent and reduction kinetics. New capabilities and future directions are also highlighted.

CONSPECTUS Gold nanostructures have garnered considerable attention in recent years for their potential to enhance both the diagnosis and treatment of cancer through their advantageous chemical and physical properties. The key feature of Au nanostructures for enabling this diverse array of biomedical applications is their attractive optical properties, i.e. the scattering and absorption of light at resonant wavelengths due to the excitation of plasmon oscillations. This phenomenon is commonly known as localized surface plasmon resonance (LSPR) and is the source of the ruby red color of conventional Au colloids. The resonant wavelength is highly dependent on the size, shape, and geometry of the nanostructures, providing a set of knobs to maneuver the optical properties as needed. For in vivo applications, especially when optical excitation or transduction is involved, the LSPR peaks of the Au nanostructures have to be tuned to the transparent window of soft tissues in the near-infrared (NIR) region (from 700–900 nm) in order to maximize the penetration depth. One class of nanostructures with tunable LSPR peaks in the NIR region is Au nanocages. These versatile nanostructures are characterized by hollow interiors, ultrathin and porous walls, and can be prepared in relatively large quantities using a remarkably simple procedure based on the galvanic replacement between Ag nanocubes and aqueous chloroauric acid. The LSPR peaks of Au nanocages can be readily and precisely tuned to any wavelength in the NIR region by controlling their size and/or wall thickness. Other significant features of Au nanocages that make them particularly intriguing materials for biomedical applications include their compact sizes, large absorption cross sections (almost five orders of magnitude greater than those of conventional organic dyes), bio-inertness, as well as a robust and straightforward procedure for surface modification based on the Au-thiolate chemistry. In this article, we present some of the most recent advances in the use of Au nanocages for a broad range of theranostic applications, including their use: i) as tracers for tracking by multi-photon luminescence; ii) as contrast agents for photoacoustic (PA) and mutimodal (PA/fluorescence) imaging; iii) as photothermal agents for the selective destruction of cancerous or diseased tissue; and iv) as drug delivery vehicles for controlled and localized release in response to external stimuli such as NIR radiation or high-intensity focused ultrasound (HIFU).

Nanoscale Pt-Ni bimetallic octahedra with controlled sizes have been actively explored in recent years owning to their outstanding activity for the oxygen reduction reaction (ORR). Here we report the synthesis of uniform 9 nm Pt-Ni octahedra with the use of oleylamine and oleic acid as surfactants and W(CO)6 as a source of CO that can promote the formation of {111} facets in the presence of Ni. Through the introduction of benzyl ether as a solvent, the coverage of both surfactants on the surface of resultant Pt-Ni octahedra was significantly reduced while the octahedral shape was still attained. By further removing the surfactants through acetic acid treatment, we observed a specific activity 51-fold higher than that of the state-of-the-art Pt/C catalyst for the ORR at 0.93 V, together with a record high mass activity of 3.3 A mgPt(-1) at 0.9 V (the highest mass activity reported in the literature was 1.45 A mgPt(-1)). Our analysis suggests that this great enhancement of ORR activity could be attributed to the presence of a clean, well-preserved (111) surface for the Pt-Ni octahedra.

Controlling the shape or morphology of metal nanocrystals is central to the realization of their many applications in catalysis, plasmonics, and electronics. In one of the approaches, the metal nanocrystals are grown from seeds of certain crystallinity through the addition of atomic species. In this case, manipulating the rates at which the atomic species are added onto different crystallographic planes of a seed has been actively explored to control the growth pattern of a seed and thereby the shape or morphology taken by the final product. Upon deposition, however, the adsorbed atoms (adatoms) may not stay at the same sites where the depositions occur. Instead, they can migrate to other sites on the seed owing to the involvement of surface diffusion, and this could lead to unexpected deviations from a desired growth pathway. Herein, we demonstrated that the growth pathway of a seed is indeed determined by the ratio between the rates for atom deposition and surface diffusion. Our result suggests that surface diffusion needs to be taken into account when controlling the shape or morphology of metal nanocrystals. seeded growth | shape control | noble metals S urface diffusion is a general process that involves the motion of adsorbed atoms (adatoms), molecules, or atomic clusters on the surface of a solid material (1, 2). Over the past decades, it has emerged as an important concept in many areas of surface science, including catalysis, epitaxial growth, and electromigration of voids (3-7). Here, we demonstrated that surface diffusion also plays a pivotal role in determining the growth pathway of a seed and thus the shape or morphology taken by the final product in a solutionphase synthesis of metal nanocrystals. Fig. 1 schematically illustrates four possible pathways for the growth of a cubic seed. As a model system, we focused on Pd nanocubes with slight truncation at corners and edges, together with six side faces passivated by chemisorbed Br -ions. In the following discussion, we refer to them as "Pd cubic seeds" for simplicity. We chose them as seeds for two major reasons: (i) they had a well-defined shape, together with a set of low-index facets on the surface (8, 9); and (ii) their side faces are blocked by Br -ions to ensure selective deposition of atoms onto the corner sites during seed-mediated growth (10-12). These two distinctive features allowed us to easily track the deposition of atoms and their surface diffusion during a growth process by analyzing the shape or morphology of the final product.The newly formed Pd atoms resulting from the reduction of a Pd precursor are expected to deposit at the corners of a cubic seed because the side faces are blocked by the chemisorbed Br -ions (Fig. 1A, 1). Upon deposition, there will be two different options for these adatoms: staying at the corner sites or migrating to other sites, including edges and side faces, through surface diffusion (Fig. 1A, 2 and 3). It should be pointed out that only surface diffusion was allowed here to move atoms from corners to edg...

This article presents a quantitative analysis of the role played by poly(vinyl pyrrolidone) (PVP) in seed-mediated growth of Ag nanocrystals. Starting from Ag nanocubes encased by {100} facets as the seeds, the resultant nanocrystals could take different shapes depending on the concentration of PVP in the solution. If the concentration was above a critical value, the seeds simply grew into larger cubes still enclosed by {100} facets. When the concentration fell below a critical value, the seeds would evolve into cuboctahedrons enclosed by a mix of {100} and {111} facets and eventually octahedrons completely covered by {111} facets. We derived the coverage density of PVP on Ag(100) surface by combining the results from two measurements: i) cubic seeds were followed to grow at a fixed initial concentration of PVP to find out when {111} facets started to appear on the surface; and ii) cubic seeds were allowed to grow at reduced initial concentrations of PVP to see at which concentration {111} facets started to appear from the very beginning. We could calculate the coverage density of PVP from the differences in PVP concentration and the total surface area of Ag nanocubes between these two samples. The coverage density was found to be 140 and 30 repeating units per nm2 for PVP of 55,000 and 10,000 g/mol in molecular weight, respectively, for cubic seeds of 40 nm in edge length. These values dropped slightly to 100 and 20 repeating units per nm2, respectively, when 100-nm Ag cubes were used as the seeds.

Peroxidase mimics with dimensions on the nanoscale have received great interest as emerging artificial enzymes for biomedicine and environmental protection. While a variety of peroxidase mimics have been actively developed recently, limited progress has been made toward improving their catalytic efficiency. In this study, we report a type of highly efficient peroxidase mimic that was engineered by depositing Ir atoms as ultrathin skins (a few atomic layers) on Pd nanocubes (i.e., Pd-Ir cubes). The Pd-Ir cubes exhibited significantly enhanced efficiency, with catalytic constants more than 20- and 400-fold higher than those of the initial Pd cubes and horseradish peroxidase (HRP), respectively. As a proof-of-concept demonstration, the Pd-Ir cubes were applied to the colorimetric enzyme-linked immunosorbent assay (ELISA) of human prostate surface antigen (PSA) with a detection limit of 0.67 pg/mL, which is ∼110-fold lower than that of the conventional HRP-based ELISA using the same set of antibodies and the same procedure.