According to the cement sulfate corrosion resistance properties of Portland cement mixed burning shale to determine the erosion test method, and analyzes the influence of different system of calcined shale sulphate corrosion resistance properties of Portland cement. The results show that: calcined shale during 800 to 900 ℃, 60min ~ 120min mixed into Portland cement, can improve the sulfate resistance of cement resistance in different degree, shale calcined during 850 ℃and 120min mixed into Portland cement, corrosion resistance coefficient of cement is 1.25. Through XRD testing means, hydrate of hardened cement paste are analyzed, compared with Portland cement mixed with calcined shale, visible after C-S-H diffraction peaks of cement hydrates phase enhancement, and Ca(OH) 2 peak decreased. Using the scanning electron microscope on the part of the corrosion morphology after mortar were observed, visible cement stone in Aft generation, generation of a small amount of Aft to make the structure of cement stone is more compact, beneficial to improve the ability of anti penetration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.