The presented study compares the structure of hexamethyldisiloxane (HMDSO) and hexamethyldisilazane (HMDSN) plasma polymer thin films with a thickness of about 30 nm before and after a plasma oxidation process, focusing on the analysis of porosity and the correlated electrolyte up-take in the formed
The influence of ultra-thin SiOx plasma deposited films on the corrosion resistance of adhesive films on a laser surface melted 7075 aluminium alloy was investigated by means of complementary techniques in comparison to the just laser surface melted state. Laser surface melting (LSM) was performed using a continuous wave mode at a wavelength of 1064 nm. Ultra-thin plasma polymer films were deposited from a mixture of hexamethyldisilane (HMDSO), oxygen, and argon by means of an audio-frequency glow discharge. The surface morphology and surface chemistry compositions were investigated by employing field emission scanning electron microscopy, energy-dispersive X-ray spectroscopy (EDX), diffuse reflection infrared Fourier transform spectroscopy, and X-ray photoelectron spectroscopy. The corrosion resistance of plasma polymer coated LSM Al-7075 alloy was studied using linear sweep voltammetry and electrochemical impedance spectroscopy in a chloride-containing electrolyte. The electrochemical studies showed an improved corrosion resistance for plasma film-coated alloys compared to the just laser surface melted state. To study the corresponding surface adhesive properties, the samples were coated with an epoxy amine adhesive. 90°-peel test under humid conditions confirmed the improvement of interfacial wet-adhesion corrosion tests showed a strong improvement of the delamination resistance of adhesives caused by the ultra-thin interfacial SiOx-films.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.