A facile method is reported to prepare nanocellulose fibers from oil palm trunk fibers. The fibers were pretreated 2 hours with NaOH/urea solution, and the fully swelled fibers were mechanically treated through highpressure homogenization to obtain nanocellulose. The nanocellulose fibers were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction analysis (XRD), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). FTIR results revealed that there was no obvious difference between the spectra of the bleached fibers (BF), pretreated cellulose fibers (PCF), and cellulose nanofibers (NCF), which indicated that the pretreatment process is a non-derivative reaction. The crystallinity of PCF and NCF decreased and contained the cellulose I crystal structure. The PCF presented both a distorted structure and a coarser surface. The resulting NCF were approximately 10 nm to 100 nm in diameter with the length varying from hundreds of nanometers to several micrometers, as observed by SEM. The thermal degradation of NCF was 223 °C with about 20% weight loss, and the maximum degradation temperature was 338 °C. NaOH/urea showed potential as a mild solvent for preparing nanocellulose fibers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.