The present research aimed to develop natural rubber (NR) hybrid composites reinforced with calcium carbonate/carbon black (CC/CB) and calcium carbonate/silica (CC/SC). The influence of CC/CB and CC/SC with various filler ratios (120/0, 90/5, 60/10, 30/15 and 0/20) on cure characteristics and mechanical properties of the vulcanizates was investigated and their reinforcing efficiency was compared. It has been found that incorporation of CB in the hybrid filler decreases the scorch time and cure time but increases crosslink density, whereas the incorporation of silica showed cure retardation. As CB or SC content increases, stiffness, tensile strength and tear strength increase, while elongation at break and compression set decrease. Scanning electron microscopy studies also reveal poor filler dispersion and poor adhesion between filler particles and matrix in the vulcanizates with increasing in CC content in a weight filler ratio which causes inferior mechanical properties. Incorporation of CB or SC content enhanced the mechanical properties of the vulcanizates, where CC/CB hybrid system exhibited higher reinforcing efficiency compared with CC/SC hybrid system.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.