The effect of different surface finishes, electroless nickel immersion gold (ENIG) and electroless nickel electroless palladium immersion gold (EN-EPIG), on the mechanical properties of Sn-58Bi bumps made with solder paste enhanced with epoxy were investigated. The microstructure and fracture surfaces were observed with scanning electron microscopy, and the compositions of the IMC and solder were measured using energy dispersive spectrometry and an electron probe micro-analyzer (EPMA). To evaluate the mechanical properties, low-speed shear tests and board-level drop tests were performed. The result of the shear tests showed that the bonding strength of the epoxy-enhanced Sn-58Bi solder bumps was higher than that of Sn-58Bi solder for all surface finishes, because of the epoxy surrounding the solder, and the fracture surfaces of epoxy-enhanced Sn-58Bi indicated ductile fracture in the solder joint. However, the result of the drop tests showed that samples with the ENIG and ENEPIG surface finishes had lower drop numbers compared to the sample without these surface finishes. The lower performance resulted from insufficient ejection of epoxy from the ENIG and ENEPIG surface finishes during reflow, which reduced the interfacial bonding area.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.