This research investigates plasma-treated and metal-coated carbon nanowalls (CNWs) for use as counter electrodes of dye-sensitized solar cells (DSSCs). The CNWs were synthesized on a fluorine-tin-oxide (FTO) glass substrate using the microwave plasma-enhanced chemical vapor deposition (PECVD) system with methane (CH4) gas. The post-plasma treatment was performed on the CNWs with hydrogen (H2) plasma using PECVD, and the CNWs were sputter-coated with metal films using the RF magnetron sputtering system with a four-inch tungsten (W) target. Then the post-plasma-treated and metal-coated CNWs were used as counter electrodes for the fabrication of the DSSCs. Field-emission scanning electron microscopy (FE-SEM) was performed to obtain cross-sectional and planar images of the grown CNWs. The energy conversion efficiencies of the DSSCs manufactured using the post-plasma-treated and metal-layer-coated CNWs as the counter electrodes were measured.
To fabricate TiO 2 nanoparticle-based dye sensitized solar cells (DSSCs) at a low-temperature, DSSCs were fabricated using hydropolymer and ZnO nanoparticles composites for the electron transport layer around a low-temperature (200 o C). ZnO nanoparticle with 20 nm and 60 nm diameter were used and Pt was deposited as a counter electrode on ITO/glass using an RF magnetron sputtering. We investigate the effect of ZnO nanoparticle concentration in hydropolymer and ZnO nanoparticle solution on the photoconversion performance of the low temperature fabricated (200 o C) DSSCs. Using cis-bis(isothiocyanato)bis(2,20 bipyridy1-4,40 dicarboxylato) ruthenium (II) bis-tetrabutylammonium (N719) dye as a sensitizer, the corresponding device performance and photo-physical characteristics are investigated through conventional physical characterization techniques. The effect of thickness of the ZnO photoelectrode and the morphology of the ZnO nanoparticles with the variations of hydropolymer to ZnO ratio on the photoconversion performance are also investigated. The morphology of the ZnO layer after sintering was examined using a field emission scanning electron microscope (FE-SEM). 60 nm ZnO nanoparticle DSSCs showed an incident photon-to-current conversion efficiency (IPCE) value of about 7% higher than that of 20 nm ZnO nanoparticle DSSCs. The maximum parameters of the short circuit current density (J sc), the open circuit potential (V oc), fill factor (ff), and efficiency (η) in the 60 nm ZnO nanoparticle-based DSSC devices were 4.93 mA/cm 2 , 0.56V, 0.40, and 1.12%, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.