Secondary caries is one of the important issues related to using dental composite restorations. Effective prevention of cariogenic bacteria survival may reduce this problem. The aim of this study was to evaluate the antibacterial activity and physical properties of composite materials with silver sodium hydrogen zirconium phosphate (SSHZP). The antibacterial filler was introduced at concentrations of 1%, 4%, 7%, 10%, 13%, and 16% (w/w) into model composite material consisting of methacrylate monomers and silanized glass and silica fillers. The in vitro reduction in the number of viable cariogenic bacteria Streptococcus mutans ATCC 33535 colonies, Vickers microhardness, compressive strength, diametral tensile strength, flexural strength, flexural modulus, sorption, solubility, degree of conversion, and color stability were investigated. An increase in antimicrobial filler concentration resulted in a statistically significant reduction in bacteria. There were no statistically significant differences caused by the introduction of the filler in compressive strength, diametral tensile strength, flexural modulus, and solubility. Statistically significant changes in degree of conversion, flexural strength, hardness (decrease), solubility (increase), and in color were registered. A favorable combination of antibacterial properties and other properties was achieved at SSHZP concentrations from 4% to 13%. These composites exhibited properties similar to the control material and enhanced in vitro antimicrobial efficiency.
Colonization of silicone-based soft lining materials by pathogenic yeast-type fungi is a common problem associated with the use of dentures. In this study, silver sodium hydrogen zirconium phosphate (SSHZP) was introduced into polydimethylsiloxane-based material as an antimicrobial filler at concentrations of 0.25, 0.5, 1, 2, 4, 6, 8, 10, 12, and 14% (w/w). The in vitro antimicrobial efficacy was investigated. Candida albicans was used as a characteristic representative of pathogenic oral microflora. Staphylococcus aureus and Escherichia coli were used as the typical Gram-positive and Gram-negative bacterial strains, respectively. The effect of filler addition on the Shore A hardness, tensile strength, tensile bond strength, sorption, and solubility was investigated. An increase in the filler concentration resulted in an increase in hardness, sorption, and solubility, and for the highest concentration, a decrease in bond strength. The favorable combination of antimicrobial efficacy with other properties was achieved at filler concentrations ranging from 2% to 10%. These composites exhibited mechanical properties similar to the material without the antimicrobial filler and enhanced in vitro antimicrobial efficiency.
The colonization of poly(methyl methacrylate) (PMMA) denture base materials by pathogenic microorganisms is a major problem associated with the use of prostheses, and the incorporation of antimicrobial fillers is a method of improving the antimicrobial properties of these materials. Numerous studies have demonstrated the initial in vitro antimicrobial effectiveness of this type of material; however, reports demonstrating the stability of these fillers over longer periods are not available. In this study, silver sodium hydrogen zirconium phosphate was introduced into the powder component of a PMMA denture base material at concentrations of 0.25%, 0.5%, 1%, 2%, 4%, and 8% (w/w). The survival rates of the gram-positive bacterium Staphylococcus aureus, gram-negative bacterium Escherichia coli and yeast-type fungus Candida albicans were established after fungal or bacterial suspensions were incubated with samples that had been previously stored in distilled water. Storage over a three-month period led to the progressive reduction of the initial antimicrobial properties. The results of this study suggest that additional microbiological tests should be conducted for materials that are treated with antimicrobial fillers and intended for long-term use. Future long-term studies of the migration of silver ions from the polymer matrix and the influence of different media on this ion emission are required.
Colonization of polymeric dental prosthetic materials by yeast-like fungi and the association of these microorganisms with complications occurring during prosthetic treatment are important clinical problems. In previously presented research, submicron inorganic particles of silver sodium hydrogen zirconium phosphate (S-P) were introduced into poly(methyl methacrylate) (PMMA) denture base material which allowed for obtaining the antimicrobial effect during a 90 day experiment. The aim of the present study was to investigate the flexural strength, impact strength, hardness, wear resistance, sorption, and solubility during three months of storage in distilled water. With increasing S-P concentration after 2 days of conditioning in distilled water, reduced values of flexural strength (107-72 MPa), impact strength (18.4-5.5 MPa) as well as enhanced solubility (0.95-1.49 µg/mm 3 ) were registered, but they were at acceptable levels, and the sorption was stable. Favorable changes included increased hardness , flexural modulus (2.9-3.3 GPa), and decreased volume loss during wear test (2.9-0.2 mm 3 ). The percentage changes of the analyzed properties during the 90 days of storage in distilled water were similar for all materials.
Yeast-like fungi such as Candida albicans (C. albicans) are the primary pathogenic microorganism in the oral cavity of denture wearers. The research available so far, conducted according to a protocol based on the exposure of specimens to a C. albicans suspension and their cutting with water cooling, shows that hard polymethyl methacrylate (PMMA) prosthetic materials are not only surface colonized, but also penetrated by microorganisms in a short time. This justifies the hypothesis that exposure to a suspension of the C. albicans strain causes the changes in mechanical properties due to surface colonization and/or penetration of the samples. In the current study, the chosen mechanical properties (flexural strength, flexural modulus, tensile strength, impact strength, ball indentation hardness, and surface Vickers hardness at 300 g load) of the PMMA denture base material Vertex RS (Vertex-Dental, The Netherlands) exposed for 30, 60, and 90 days to a suspension of C. albicans were investigated. The potential penetration of yeast was examined on the fractured surfaces (interior of specimens) to eliminate the risk of the contamination of samples during cutting. There was no influence on the flexural strength, flexural modulus, tensile strength, impact strength, or ball indentation hardness, but a significant decrease in surface hardness was registered. Microscopic observations did not confirm the penetration of C. albicans. On the surface, blastospores and pseudohyphae were observed in crystallized structures and in traces after grinding, which indicates that in clinical conditions, it is not penetration but the deterioration of surface quality, which may lead to the formation of microareas that are difficult to disinfect, causing rapid recolonization.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.